Effect of High-Pressure Oxygen Annealing on Electrical and Magnetoelectric Properties of BaSrCo2Fe11AlO22 Ceramics

被引：0

作者：

20151600746824

机构：

[1] Hirose, Sakyo

[2] Haruki, Kohei

[3] Ando, Akira

[4] Kimura, Tsuyoshi

来源：

Hirose, Sakyo (h_sakyo@murata.com) | 1600年 / Blackwell Publishing Inc., Postfach 10 11 61, 69451 Weinheim, Boschstrabe 12, 69469 Weinheim, Deutschland, 69469, Germany卷

关键词：

The effect of high-pressure oxygen (HPO) annealing on the electrical; magnetic; and magnetoelectric (ME) properties of room-temperature multiferroic BaSrCo2Fe11AlO22 ceramics was investigated. The electrical resistivity of the ceramics was found to strongly depend on the partial oxygen pressure during annealing at 1040°C. Samples annealed under ~10 atm of oxygen exhibited a resistivity of up to 1.6 × 109 Ω·cm at room temperature; more than two orders of magnitude higher than that of samples without oxygen annealing. Thermally stimulated current and complex impedance measurements suggested that the enhancement of the resistivity by the HPO annealing originated from a decrease in the amount of defects related to oxygen vacancies and an increase in the resistance of grains and interfaces. HPO annealing also affects the magnetic-field response of spiral magnetic ordering; which is ascribed to the ME properties. Furthermore; samples subjected to HPO annealing exhibited a lower contribution of the space charges trapped at the grain boundaries and/or defects to the magnitude of the measured magnetoelectrically induced electric polarization P. The present results indicate that HPO annealing is an effective method to evaluate authentic ME effects in multiferroic BaSrCo2Fe11AlO22 ceramics. © 2015 The American Ceramic Society;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

引用

共 50 条

[31] The effect of oxygen vacancies and aluminium substitution on the high-pressure properties of brownmillerite-structured Ca2Fe2−xAlxO5
Carine B. Vanpeteghem
Ross J. Angel
Jing Zhao
Nancy L. Ross
Günther J. Redhammer
Friedrich Seifert
Physics and Chemistry of Minerals, 2008, 35 : 493 - 504
[32] Thermal Annealing Effect on the Thermoluminescence Properties of Commercial High-Pressure High-Temperature Diamond Powders
Claudia Calderon-Martinez, Maria
Ines Gil-Tolano, Maria
Cruz-Zaragoza, Epifanio
Melendrez, Rodrigo
Chernov, Valery
Barboza-Flores, Marcelino
PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 2023, 220 (04):
[33] Effect of high-pressure torsion on the microstructure and thermoelectric properties of Fe2VAl-based compounds
2018, American Institute of Physics Inc. (124)
[34] Effect of annealing under N2 atmosphere on electrical fatigue properties of PLZT ceramics
Zhang, JB
Yue, ZX
Li, LT
RARE METAL MATERIALS AND ENGINEERING, 2003, 32 : 366 - 369
[35] Crystal Growth and Investigation of High-Pressure Physical Properties of Fe2As
Dai, Guangyang
Zhang, Changling
Zhang, Sijia
He, Xin
Ren, Chongwen
Zhao, Jianfa
Li, Xiaodong
Wang, Xiancheng
Jin, Changqing
CRYSTALS, 2020, 10 (09): : 1 - 7
[36] Effect of high-pressure D2 and H2 annealing on LFN properties in FD-SOI pTFET
Hyun-Jin Shin
Sunil Babu Eadi
Yeong-Jin An
Tae-Gyu Ryu
Do-woo Kim
Hi-Deok Lee
Hyuk-Min Kwon
Scientific Reports, 12
[37] Effect of high-pressure D2 and H2 annealing on LFN properties in FD-SOI pTFET
Shin, Hyun-Jin
Eadi, Sunil Babu
An, Yeong-Jin
Ryu, Tae-Gyu
Kim, Do-Woo
Lee, Hi-Deok
Kwon, Hyuk-Min
SCIENTIFIC REPORTS, 2022, 12 (01)
[38] Effect of High-Pressure Annealing on ALD HfO2/Si Interfacial Layer
Ahn, Seungjoon
Kim, Ho Seob
Kim, Dae-Wook
Oh, Tae-Sik
Hang, Dong Hwan
Ahn, Seong Joon
JOURNAL OF NANOELECTRONICS AND OPTOELECTRONICS, 2016, 11 (02) : 210 - 213
[39] Effect of annealing temperature on microstructure and properties of stainless steel rings after high-pressure torsion
Volokitina, I. E.
Volokitin, A. V.
METALLURGIST, 2024, 68 (01) : 52 - 58
[40] HIGH-PRESSURE AND TEMPERATURE EFFECT ON ELECTRICAL PROPERTIES OF P-TYPE GALLIUM ANTIMONIDE
SIROTA, NN
SHIPILO, VB
PHYSICA STATUS SOLIDI, 1968, 25 (01): : K23 - &

← 1 2 3 4 5 →