High-temperature oxidation of intermetallics based on Ti-Al-Si system

被引：0
|
作者：
Knaislová A. [1 ]
Šimůnková V. [1 ]
Novák P. [1 ]
机构：
[1] Department of Metals and Corrosion Engineering, University of Chemistry and Technology Prague, Technická 5, Prague
来源：
Knaislová, Anna (knaisloa@vscht.cz) | 2018年 / Jan-Evangelista-Purkyne-University卷 / 18期
关键词：
Intermetallics; Parabolic constant; Reactive sintering; Thermal stability;
D O I：
10.21062/ujep/87.2018/a/1213-2489/MT/18/2/255
中图分类号：
学科分类号：
摘要：
Ti-Al-Si alloys excel with their low density and good resistance against high-temperature oxidation in comparison with so far commonly used nickel alloys. Silicon in Ti-Al-Si alloys has significant positive effect on hightemperature oxidation due to increasing adhesion of oxide layer. The TiAl20Si20 alloy was evaluated as the best alloy from tested ones, because its oxide layer protected very well the basic material and TiAl20Si20 achieved good hardness after 400 hours of annealing. © 2018. Published by Manufacturing Technology.
引用
收藏
页码：255 / 258
页数：3
相关论文
共 50 条
  • [31] Unidirectional crystallization and high-temperature oxidation of in situ Ti3(Al,Si)-Ti5(Si,Al)3 composite
    Vojtech, D.
    Novak, M.
    Novak, P.
    Lejcek, P.
    Kopecek, J.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 489 (1-2): : 1 - 10
  • [32] Microstructure and super oxidation resistance of the network structured Ti-Al-Si coating
    Li, X. T.
    Huang, L. J.
    Jiang, S.
    Gao, Y. N.
    An, Q.
    Wang, S.
    Zhang, R.
    Geng, L.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 807
  • [33] Structure and mechanical properties of powder materials of the system Ti-Al-Si
    Ban'kovskii, OI
    Kulak, LD
    Kuz'menko, NN
    Firstov, SA
    POWDER METALLURGY AND METAL CERAMICS, 2000, 39 (5-6) : 310 - 316
  • [34] DIRECTIONAL CRYSTALLIZATION OF TI-AL-SI EUTECTICS
    Vojtech, Dalibor
    Lejcek, Pavel
    Kopecek, Jaromir
    Bialasova, Katrin
    METAL 2009, CONFERENCE PROCEEDINGS, 2009, : 344 - 350
  • [35] THE BETA-TI(AL,SI)+TI5(SI,AL)3 EUTECTIC REACTION IN THE TI-AL-SI TERNARY-SYSTEM
    WU, JS
    QIU, GH
    ZHANG, LT
    SCRIPTA METALLURGICA ET MATERIALIA, 1994, 30 (02): : 213 - 218
  • [36] Effect of Si and Al additions on the high-temperature oxidation behavior of Si-based alloys
    Lin, S.E.
    Tsai, C.H.
    Kai, W.
    Journal of Chinese Corrosion Engineering, 2012, 26 (03): : 129 - 140
  • [37] High temperature oxidation of Ti-48%Al-2%W intermetallics
    Shim, WS
    Lee, DB
    METALS AND MATERIALS INTERNATIONAL, 2003, 9 (05) : 473 - 477
  • [38] Synthesis of Intermediary Phases in Ti-Al-Si System by Reactive Sintering
    Novak, Pavel
    Vojtech, Dalibor
    Serak, Jan
    Kubasek, Jiri
    Prusa, Filip
    Knotek, Vitezslav
    Michalcova, Alena
    Novak, Michal
    CHEMICKE LISTY, 2009, 103 (12): : 1022 - 1026
  • [39] Structure and mechanical properties of sintered materials in the Ti-Al-Si system
    Ban'kovskij, O.I.
    Kulak, L.D.
    Kuz'menko, N.N.
    Firstov, S.A.
    Poroshkovaya Metallurgiya, 2000, (5-6): : 108 - 116
  • [40] HIGH-TEMPERATURE OXIDATION OF Ti-Al-Ta AND Ti-Al-Nb ALLOYS
    Popela, Tomas
    Vojtecha, Dalibor
    Novak, Pavel
    Knotek, Vitezslav
    Prusa, Filip
    Michalcova, Alena
    Novak, Michal
    Serak, Jan
    METAL 2010: 19TH INTERNATIONAL METALLURGICAL AND MATERIALS CONFERENCE, 2010, : 834 - 837
12345