Repair of fatigue cracks initiated around box weldes by using low-transformation temperature welding material

被引：0
|
作者：
Suzuki, Naoyuki [1 ]
Ohta, Akihiko [1 ]
Maeda, Yoshio [1 ]
机构：
[1] Natl. Inst. for Materials Science
来源：
Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society | 2003年 / 21卷 / 01期
关键词：
Compressive residual stresses - Welded joints;
D O I：
10.2207/qjjws.21.62
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：62 / 67
相关论文
共 46 条
  • [41] Microstructure, residual stress and mechanical properties of a high strength steel weld using low transformation temperature welding wires
    Chen, Xizhang
    Fang, Yuanyuan
    Li, Peng
    Yu, Zhenzhen
    Wu, Xiaodong
    Li, Dongsheng
    MATERIALS & DESIGN, 2015, 65 : 1214 - 1221
  • [42] Investigation of the Residual Stress in a Multi-Pass T-Welded Joint Using Low Transformation Temperature Welding Wire
    Feng, Zhongyuan
    Ma, Ninshu
    Tsutsumi, Seiichiro
    Lu, Fenggui
    MATERIALS, 2021, 14 (02) : 1 - 15
  • [43] Corrigendum to Fatigue life improvement using low transformation temperature weld material with measurement of residual stress [Int. J. Fatigue 164 (2022) 107137] (International Journal of Fatigue (2022) 164, (S0142112322003930), (10.1016/j.ijfatigue.2022.107137))
    Franks, Jordan
    Wheatley, Greg
    Zamani, Pedram
    Nejad, Reza Masoudi
    Macek, Wojciech
    Branco, Ricardo
    International Journal of Fatigue, 2024, 183
  • [44] Extraction of Low-Dimensional Structures of Noble and Rare Metals from Carbonaceous Ores Using Low-Temperature and Energy Impacts at Succeeding Stages of Raw Material Transformation
    Aleksandrova, Tatiana
    Nikolaeva, Nadezhda
    Afanasova, Anastasia
    Romashev, Artyem
    Aburova, Valeriya
    Prokhorova, Evgeniya
    MINERALS, 2023, 13 (01)
  • [45] Confirmation of tensile residual stress reduction in electron beam welding using low transformation temperature materials (LTT) as localized metallurgical injection - Part 1: Metallographic analysis
    Gach, Stefan
    Schwedt, Alexander
    Olschok, Simon
    Reisgen, Uwe
    Mayer, Joachim
    MATERIALS TESTING, 2017, 59 (02) : 148 - 154
  • [46] Confirmation of tensile residual stress reduction in electron beam welding using low transformation temperature materials (LTT) as localized metallurgical injections - Part 2: Residual stress measurement
    Gach, Stefan
    Olschok, Simon
    Francis, John Anthony
    Reisgen, Uwe
    MATERIALS TESTING, 2017, 59 (7-8) : 618 - 624
12345