Microstructure evolution during silicon oxidation at room temperature under composite ion beam irradiation

被引：0
|
作者：
Prikhodko, K.E. [1 ,2 ]
Gurovich, B.A. [1 ]
Komarov, D.A. [1 ]
Goncharova, D.A. [1 ]
Kutuzov, L.V. [1 ]
机构：
[1] National Research Centre, Kurchatov Institute, Kurchatov sq.1, Moscow,123182, Russia
[2] National Research Nuclear University (MEPhI), Kashirskoe sh., 31, 115409, Russia
来源：
Nuclear Instruments and Methods in Physics Research, Section B: Beam Interactions with Materials and Atoms | 2014年 / 326卷
关键词：
Ions;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this work, we studied the silicon microstructure evolution during its oxidation under composite beam ion irradiation at room temperature. It was found that when the composite ion beam was formed by hydrogen and dry oxygen mixture at low doses (∼1018cm-2), a porous silicon layer was formed. During irradiation, the pore size gradually reduced and at a dose of ∼1020cm-2pores disappear completely, and an uniform layer of silicon oxide was formed. If residual gases and hydrogen are used to generate a composite ion beam, the formation of porous silicon is not found. The final thickness of irradiation-induced silicon oxide corresponded to the projected range of protons at a given energy in both cases. © 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码：273 / 277
相关论文
共 50 条
  • [21] Oxidation of room temperature silicon(001) surfaces in a hyperthermal atomic oxygen beam
    Tagawa, M
    Ema, T
    Kinoshita, H
    Umeno, M
    Ohmae, N
    Minton, TK
    7TH INTERNATIONAL SYMPOSIUM ON MATERIALS IN SPACE ENVIRONMENT, 1997, 399 : 225 - 229
  • [22] Effect of ion irradiation on the optical properties and room temperature oxidation of copper surface
    Poperenko, LV
    Shaaban, ER
    Khánh, NQ
    Stashchuk, VS
    Vinnichenko, MV
    Yurgelevich, IV
    Nosach, DV
    Lohner, T
    THIN SOLID FILMS, 2004, 455 : 453 - 456
  • [23] MICROSTRUCTURE EVOLUTION DURING IRRADIATION
    KIRITANI, M
    JOURNAL OF NUCLEAR MATERIALS, 1994, 216 : 220 - 264
  • [24] Temperature distribution in polymeric films during ion beam irradiation
    Ide-Ektessabi, A
    Watanabe, Y
    REVIEW OF SCIENTIFIC INSTRUMENTS, 2002, 73 (02): : 849 - 851
  • [25] The room temperature oxidation of porous silicon
    Salonen, J
    Lehto, VP
    Laine, E
    APPLIED SURFACE SCIENCE, 1997, 120 (3-4) : 191 - 198
  • [26] Room temperature migration of ion beam injected point defects in crystalline silicon
    Privitera, V
    Coffa, S
    Priolo, F
    Larsen, KK
    Libertino, S
    Carnera, A
    NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1996, 120 (1-4): : 9 - 13
  • [27] Room temperature migration of ion beam injected point defects in crystalline silicon
    Privitera, V.
    Coffa, S.
    Priolo, F.
    Larsen, K.K.
    Libertino, S.
    Carnera, A.
    Nuclear Instruments and Methods in Physics Research, Section B: Beam Interactions with Materials and Atoms, 1996, 120 (1-4): : 9 - 13
  • [28] Microstructure evolution during electron and ion irradiation in commercial purity magnesium
    Khan, A. K.
    Yao, Z.
    Daymond, M. R.
    PHILOSOPHICAL MAGAZINE, 2014, 94 (17) : 1909 - 1923
  • [29] Evolution of the microstructure in nanocrystalline copper electrodeposits during room temperature storage
    Pantleon, Karen
    Somers, Marcel A. J.
    ZEITSCHRIFT FUR KRISTALLOGRAPHIE, 2007, : 261 - 266
  • [30] Microstructure Evolution of Polycrystalline Zinc during Tensile Testing at Room Temperature
    Yue, Rui
    Li, Lingyu
    Li, Ziyu
    Zhang, Jinpeng
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (14) : 7393 - 7399
12345