Environmental aging performance and mechanism of T700 carbon fiber reinforced epoxy resin matrix composites

被引：0
|
作者：
Zhang D. [1 ]
Liu G. [1 ]
Bao J. [1 ]
Tang B. [1 ]
Zhong X. [1 ]
Chen X. [1 ]
机构：
[1] Science and Technology on Advanced Composites Laboratory, Beijing Institute of Aeronautical Materials, AVIC Composite Center, Beijing
来源：
Bao, Jianwen (baojianwen@sohu.com) | 2016年 / Beijing University of Aeronautics and Astronautics (BUAA)卷 / 33期
关键词：
Carbon fiber composites; Environmental aging; Epoxy resin; Mechanical properties; Thermal property analysis;
D O I：
10.13801/j.cnki.fhclxb.20151022.002
中图分类号：
学科分类号：
摘要：
In order to verify the durability of composites, the microscopic morphology, surface element content, thermal properties and mechanical properties of T700 carbon fiber reinforced epoxy resin matrix composites were studied after environmental aging. The results show that the coaction of photo-oxidative degradation and thermo-oxidative degradation cause the T700 carbon fiber reinforced EP-A epoxy resin matrix (T700/EP-A) composites surface resin aging degradation. With the extension of environmental aging time, the glass transition temperature of T700/EP-A composites decreases gradually. After 3 years of environmental aging treatment, glass transition temperature of T700/EP-A composites decreases from 207℃(un-aged specimen) to 180℃, and to 172℃ after extending environmental aging of 5 years. Enhancing effects and damaging effects of the environmental aging process may coexist in the mechanical properties of the composites, thus resulting in different mechanical properties of T700/EP-A and T700/EP-B composites showing disparate trends. With the extension of environmental aging time, the longitudinal tensile strength of T700/EP-A and T700/EP-B composites first increases then decreases, the longitudinal flexural strength gradually increases, fluctuant longitudinal compress strength and interlaminar shear strength show no significant variation tendency. © 2016, BUAA Culture Media Group Ltd. All right reserved.
引用
收藏
页码：1390 / 1399
页数：9
相关论文
共 20 条
  • [1] Chen X.B., Development of advanced polymer composites, Journal of Aeronautical Materials, 20, 1, pp. 46-54, (2000)
  • [2] Chen Y.L., Liu X., Progress of aging performance research of polymer matrix composites, Equipment Environmental Engineering, 7, 4, pp. 49-56, (2010)
  • [3] Lyu X.J., Zhang Q., Ma Z.Q., Et al., Study of hydrothermal aging effect on mechanical properties of carbon fiber/epoxy resin composites, Journal of Materials Engineering, 11, pp. 50-53, (2005)
  • [4] Guo M.L., Zhao Y., Xu F.H., Et al., Study of aging of advanced polymer matrix composites I. Thermooxidizing aging, Acta Aeronautica et Astronautica Sinica, 21, pp. 62-65, (2000)
  • [5] Candido G.M., Costa M.L., Rezende M.C., Et al., Hygrothermal effects on quasi-isotropic carbon epoxy laminates with machined and molded edges, Composites Part B: Engineering, 39, 3, pp. 490-496, (2008)
  • [6] Feng Q., Li M., Gu Y.Z., Et al., Experimental research on hygrothermal properties of carbon fiber/epoxy resin composite under different hygrothermal conditions, Acta Materiae Compositae Sinica, 27, 6, pp. 16-20, (2010)
  • [7] Huang L.G., Yang Z.Z., Yan H., Et al., Study on alkali resistance of composites, Fiber Composites, 1, pp. 45-48, (2008)
  • [8] Zhan M.S., Liu D.S., Acid rain cycling aging properties and mechanism of unidirectional glass fiber reinforced epoxy composites, Fiber Reinforced Plastics/Composites, 3, pp. 28-32, (2007)
  • [9] Shokrieh M.M., Bayat A., Effects of ultraviolet radiation on mechanical properties of glass/polyester composites, Journal of Composite Materials, 41, 20, pp. 2443-2455, (2007)
  • [10] Xu Y.J., Zhao Y., Tang B.J., Et al., Effects of UVA irradiation on properties of carbon fiber reinforced epoxy resin composites indoor, Acta Materiae Compositae Sinica, 30, 2, pp. 63-69, (2013)
12