Estimation of corrosion fatigue life by evaluation on corrosion pit damage in gas turbine compressor blades under service conditions

被引：0
|
作者：
Hitachi Works, Hitachi Ltd., Saiwai-Cho, Hitachi, 317-8511, Japan [1 ]
不详 [2 ]
不详 [3 ]
机构：
来源：
Zairyo | 2013年 / 6卷 / 383-389期
关键词：
D O I：
10.2472/jsms.62.383
中图分类号：
学科分类号：
摘要：
引用
收藏
相关论文
共 50 条
  • [21] CORROSION-DAMAGE TO TURBINE NOZZLE BLADES IN CONTACT WITH NATURAL-GAS COMBUSTION PRODUCTS.
    Akimov, L.M.
    Shchurovskii, V.A.
    Romanov, E.P.
    Mikhalev, M.S.
    Baldin, A.V.
    Matvienko, A.F.
    Soviet Energy Technology (English translation of Energomashinostroenie), 1984, (10): : 35 - 41
  • [22] Evaluation of the operating conditions of gas turbine blades and vanes after long term service
    Auerkari, Pertti
    Salonen, Jorma
    Gustafsson, Tom E.
    Karvonen, Ilkka
    Tanttari, Heikki
    Makinen, Sari
    BALTICA VII: LIFE MANAGEMENT AND MAINTENANCE FOR POWER PLANTS, VOL 2, 2007, 247 : 25 - +
  • [23] QUANTIFICATION OF LOW-CYCLE FATIGUE LIFE FOR A GAS TURBINE COMPRESSOR VANE CARRIER UNDER VARYING OPERATING CONDITIONS
    Han, Zixi
    Jiang, Zixian
    Ehrt, Sophie
    Li, Mian
    PROCEEDINGS OF THE ASME TURBO EXPO: TURBOMACHINERY TECHNICAL CONFERENCE AND EXPOSITION, VOL 10B, 2020,
  • [24] High temperature corrosion influence on deformation and damage mechanisms in turbine blades made of IN-792 during service
    Kanesund, Jan
    Brodin, Hakan
    Johansson, Sten
    ENGINEERING FAILURE ANALYSIS, 2020, 110
  • [25] A novel approach for corrosion fatigue life estimation under asymmetric cyclic loadings using intrinsic damage dissipation
    Li, Haoran
    Xiang, Zhong
    Li, Wenqi
    Peng, Yan
    Ren, Zhongkai
    ENGINEERING FAILURE ANALYSIS, 2024, 157
  • [26] A STUDY OF THE INFLUENCE OF SERVICE OPERATING TIME AND A CORROSIVE MEDIUM ON THE LIFE OF GAS-TURBINE ENGINE COMPRESSOR BLADES
    TROSHCHENKO, VT
    PROKOPENKO, AV
    TORGOV, VN
    BAUMSHTEIN, MV
    GETSOV, LB
    STRENGTH OF MATERIALS, 1981, 13 (04) : 401 - 407
  • [27] Long term effect of power system unbalance on the corrosion fatigue life expenditure of low pressure turbine blades
    Tsao, TP
    Lin, CH
    IEE PROCEEDINGS-SCIENCE MEASUREMENT AND TECHNOLOGY, 2000, 147 (05) : 229 - 236
  • [28] Corrosion fatigue effects on life estimation of deteriorated bridges under vehicle impacts
    Zhang, W.
    Yuan, H.
    ENGINEERING STRUCTURES, 2014, 71 : 128 - 136
  • [29] Damage caused by high-temperature corrosion of gas turbine blades made of nichel-based superalloys
    Becagli, M.
    Innocenti, M.
    Fantechi, F.
    Quaderni Pignone (edizione italiana), 1988, (44): : 39 - 49
  • [30] The framework of hot corrosion fatigue life estimation of a PM superalloy using notch fatigue methodology combined with pit evolution
    Li, Zhenlei
    Li, Shaolin
    Xu, Guoqiang
    Shi, Duoqi
    Liu, Changqi
    Yang, Xiaoguang
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 153
12345