Recrystallization kinetics and microstructure evolution during annealing of cold rolled 430 stainless steel

被引：0
|
作者：
Zhang, Xiong [1 ]
Wen, Zhi [2 ]
Dou, Rui-Feng [2 ]
Zhang, Rui-Jie [3 ]
Li, Zhi-Qiang [1 ]
机构：
[1] School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China
[2] Beijing Key Laboratory for Energy Saving and Emission Reduction of Metallurgical Industry, Beijing 100083, China
[3] School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China
来源：
Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment | 2014年 / 35卷 / 01期
关键词：
Stainless steel - Activation energy - Kinetics - Cold rolling - Annealing - Metal cladding - Steel sheet;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Evolution of recrystallization microstructure and hardness of cold rolled 430 stainless steel during isothermal annealing in the range of 650°C to 875°C were studied, and the recrystallization kinetics model was established. The results show that annealing temperature has significant effect on the recrystallization incubation time and the time for complete recrystallization, the recrystallization is completed at 825°C for 5 min and at 850°C for 34 s, however, full recrystallization is not observed, in the experimental time range for the temperature lower than 800°C. Finally, the recrystallization kinetics of this material is established by JMAK type model, the values of the Avrami exponent is in the range of 0.5 to 1.0, and its activation energy is 309.12 kJ/mol.
引用
收藏
页码：212 / 216
相关论文
共 50 条
  • [31] Microstructure and texture evolution of cold-rolled deep-drawing steel sheet during annealing
    Le-yu Zhou
    Lei Wu
    Ya-zheng Liu
    Xiao-jie Cheng
    Jin-hong Sun
    International Journal of Minerals,Metallurgy and Materials, 2013, 20 (06) : 541 - 548
  • [32] Recrystallisation Characteristics of Cold Rolled Austenitic Stainless Steel during Repeated Annealing
    Kumar, B. Ravi
    Sharma, Sailaja
    RECRYSTALLIZATION AND GRAIN GROWTH V, 2013, 753 : 157 - 162
  • [33] Texture and microstructure evolution during cold rolling of a strip cast and of a hot rolled austenitic stainless steel
    Raabe, D
    ACTA MATERIALIA, 1997, 45 (03) : 1137 - 1151
  • [34] Orientation related microstructure evolution during continuous annealing of a cold-rolled low carbon steel
    Bocos, JL
    Novillo, E
    Petite, MM
    Iza-Mendia, A
    Gutierrez, I
    THERMEC'2003, PTS 1-5, 2003, 426-4 : 3581 - 3586
  • [35] Phase Transformation Kinetics During Annealing of Cold-Rolled AISI 309Si Stainless Steel
    Abdi, Ata
    Mirzadeh, Hamed
    Sohrabi, Mohammad Javad
    Naghizadeh, Meysam
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2020, 51 (05): : 1955 - 1959
  • [36] Randomization of texture during recrystallization of austenite in a cold rolled metastable austenitic stainless steel
    Chowdhury, Sandip Ghosh
    Datta, Sudarsan
    Kumar, B. Ravi
    De, P. K.
    Ghosh, R. N.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 443 (1-2): : 114 - 119
  • [37] Phase Transformation Kinetics During Annealing of Cold-Rolled AISI 309Si Stainless Steel
    Ata Abdi
    Hamed Mirzadeh
    Mohammad Javad Sohrabi
    Meysam Naghizadeh
    Metallurgical and Materials Transactions A, 2020, 51 : 1955 - 1959
  • [38] Texture evolution in cold-rolled steel during continuous annealing
    Petite, MM
    Gutiérrez, I
    BOLETIN DE LA SOCIEDAD ESPANOLA DE CERAMICA Y VIDRIO, 2000, 39 (03): : 289 - 292
  • [39] Analysis and prevention of cracking phenomena during bending of cold-rolled 430 stainless steel
    Ahn, BR
    Kim, NJ
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1998, 17 (07) : 573 - 576
  • [40] Analysis and prevention of cracking phenomena during bending of cold-rolled 430 stainless steel
    Research Inst of Industrial Science, and Technology, Pohang, Korea, Republic of
    J Mater Sci Lett, 7 (573-576):
12345