Microstructure and erosive wear properties of Ni-based alloy coating produced by plasma cladding

被引：0
|
作者：
Liu, Shenglin [1 ]
Sun, Dongbai [1 ]
Fan, Zishuan [1 ]
Wang, Guogang [1 ]
Yu, Hongying [1 ]
机构：
[1] Beijing Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China
来源：
Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing | 2007年 / 29卷 / 10期
关键词：
Cladding (coating) - Coatings - Mechanical properties - Microhardness - Microstructure - Nickel alloys - Plasma arc melting - Plasmas - Stainless steel - Wear resistance;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Using Ni46 alloy powder as the raw material, the erosive wear resistance of stainless steel was improved with Ni-based alloy coating onto the stainless steel by plasma cladding. The coating's microstructure was studied and its microhardness was measured using an HVS1000 micro-hardness tester. The erosive wear resistance of the coating in a slurry erosion tester was investigated. The results show that the mechanical properties of metal materials influenced their erosive wear resistance: the larger the hardness value of the material is, the better the anti erosive wear properties are. On the same experimental condition, the erosive wear rates of the materials follow this rule: Ni-based coating > 0Cr13Ni5Mo > 1Cr18Ni9Ti. The improvement in erosion resistance can be attributed to the solution strengthening of γ-Ni matrix and the presence of large amounts of borides and carbides which withstood the impingement of slurry erosion.
引用
收藏
页码：999 / 1004
相关论文
共 50 条
  • [21] Wear Resistance of Laser Cladding Ni-Based Alloy
    Qiu Xingwu
    Zhang Yunpeng
    Liu Chunge
    RARE METAL MATERIALS AND ENGINEERING, 2012, 41 : 182 - 185
  • [22] Microstructure and wear behavior of laser cladding Ni-based alloy composite coating reinforced by Ti(C, N) particulates
    School of Materials Science and Engineering, Shandong University, Jinan 250061, China
    不详
    China Weld Eng Ed, 2008, 3 (20-23):
  • [23] Microstructure and wear behavior of laser cladding Ni-based alloy composite coating reinforced by Ti(C,N) particulates
    齐勇田
    施瀚超
    邹增大
    胡丽萍
    China Welding, 2008, (03) : 20 - 23
  • [24] Microstructure and corrosion resistance of Ni-based alloy coating by plasma cladding on 316L stainless steel
    Peng, Zhuqin
    Wang, Hongfang
    Lu, Jinbin
    Gong, Jinxia
    Hanjie Xuebao/Transactions of the China Welding Institution, 2011, 32 (03): : 89 - 92
  • [25] Effect of Vacuum on Microstructure and Properties of Laser Cladding Ni-Based WC Coating
    Yao Yongqiang
    Lin Chen
    Shen Jingyi
    Liu Jia
    Xu Huanhuan
    LASER & OPTOELECTRONICS PROGRESS, 2019, 56 (22)
  • [26] Microstructure and Wear Properties of Laser Cladding WC/Ni-Based Composite Layer on Al-Si Alloy
    Wu, Xiaoquan
    Zhang, Daoda
    Hu, Zhi
    MATERIALS, 2021, 14 (18)
  • [27] Effect of ZrB2 on the Microstructure and Wear Resistance of Ni-Based Composite Coating Produced on Pure Ti by Laser Cladding
    Guo, Chun
    Zhou, Jiansong
    Zhao, Jierong
    Chen, Jianmin
    TRIBOLOGY TRANSACTIONS, 2011, 54 (01) : 80 - 86
  • [28] Microstructure and Mechanical Properties of Ni-Based Alloy Composite Coating on Cr12MoV by Laser Cladding
    Gao, Yali
    Tong, Yan
    Li Guohui
    Lu, Pengyong
    Zhang, Dongdong
    COATINGS, 2022, 12 (11)
  • [29] Investigation on friction and wear performance of laser cladding Ni-based alloy coating on brake disc
    Shi, Xiaoyu
    Wen, Daosheng
    Wang, Shouren
    Wang, Gaoqi
    Zhang, Mingyuan
    Li, Jinkun
    Xue, Chenglong
    OPTIK, 2021, 242 (242):
  • [30] Effects of WC-Ni content on microstructure and wear resistance of laser cladding Ni-based alloys coating
    Guo, Chun
    Chen, Jianmin
    Zhou, Jiansong
    Zhao, Jierong
    Wang, Lingqian
    Yu, Youjun
    Zhou, Huidi
    SURFACE & COATINGS TECHNOLOGY, 2012, 206 (8-9): : 2064 - 2071
12345