Microstructure and erosive wear properties of Ni-based alloy coating produced by plasma cladding

被引：0

作者：

Liu, Shenglin ^{[1
]}

Sun, Dongbai ^{[1
]}

Fan, Zishuan ^{[1
]}

Wang, Guogang ^{[1
]}

Yu, Hongying ^{[1
]}

机构：

[1] Beijing Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

来源：

Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing | 2007年 / 29卷 / 10期

关键词：

Cladding (coating) - Coatings - Mechanical properties - Microhardness - Microstructure - Nickel alloys - Plasma arc melting - Plasmas - Stainless steel - Wear resistance;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Using Ni46 alloy powder as the raw material, the erosive wear resistance of stainless steel was improved with Ni-based alloy coating onto the stainless steel by plasma cladding. The coating's microstructure was studied and its microhardness was measured using an HVS1000 micro-hardness tester. The erosive wear resistance of the coating in a slurry erosion tester was investigated. The results show that the mechanical properties of metal materials influenced their erosive wear resistance: the larger the hardness value of the material is, the better the anti erosive wear properties are. On the same experimental condition, the erosive wear rates of the materials follow this rule: Ni-based coating > 0Cr13Ni5Mo > 1Cr18Ni9Ti. The improvement in erosion resistance can be attributed to the solution strengthening of γ-Ni matrix and the presence of large amounts of borides and carbides which withstood the impingement of slurry erosion.

引用

下载

页码：999 / 1004

共 50 条

[1] Research on microstructure of Ni-based alloy coating by laser cladding
Yuan Q.
Feng X.
Cao J.
Su Z.
Zhongguo Jiguang/Chinese Journal of Lasers, 2010, 37 (08): : 2116 - 2120
[2] Effect of Cobalt on Microstructure and Wear Resistance of Ni-Based Alloy Coating Fabricated by Laser Cladding
Wang, Kaiming
Chang, Baohua
Lei, Yongping
Fu, Hanguang
Lin, Yinghua
METALS, 2017, 7 (12):
[3] Microstructure and Hardness of TiC/Ni-based Coating by Plasma Cladding
Sun Bin
Zhang Wenyong
Lu Jinbin
Wang Zhixin
MACHINERY, MATERIALS SCIENCE AND ENGINEERING APPLICATIONS, 2012, 510 : 734 - 737
[4] Microstructure and wear resistance of TaC reinforced Ni-based coating by laser cladding
Chao, Ming-Ju
Wang, Wen-Li
Liang, Er-Jun
Ouyang, Dongxun
SURFACE & COATINGS TECHNOLOGY, 2008, 202 (10): : 1918 - 1922
[5] Microstructure and Wear Properties of Ni-based Composite Coatings on Aluminum Alloy Prepared by Laser Cladding
Wu Xiaoquan
Yan Hong
Xin Yong
Yu Baobiao
Hu Zhi
Sun Yonghui
RARE METAL MATERIALS AND ENGINEERING, 2020, 49 (08) : 2574 - 2582
[6] Microstructure and Wear Properties of Ni-based Composite Coatings on Aluminum Alloy Prepared by Laser Cladding
Wu, Xiaoquan
Yan, Hong
Xin, Yong
Yu, Baobiao
Hu, Zhi
Sun, Yonghui
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2020, 49 (08): : 2574 - 2582
[7] Effect of steady magnetic field on microstructure and properties of laser cladding Ni-based alloy coating
Wang, Qian
Zhai, Lu Lu
Zhang, Liang
Zhang, Jun Wei
Ban, Chun Yan
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2022, 17 : 2145 - 2157
[8] Microstructure and wear resistance of laser cladding of Ni-based alloy on copper substrate
Wang, Yunshan
Liu, Nengwen
Zhu, Fudong
OPTOELECTRONIC MATERIALS, PTS 1AND 2, 2010, 663-665 : 1061 - 1064
[9] Effect of niobium on the microstructure and wear resistance of iron-based alloy coating produced by plasma cladding
Zhang, Limin
Sun, Dongbai
Yu, Hongying
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 490 (1-2): : 57 - 61
[10] Microstructure and Wear Resistance of in situ NbC Particles Reinforced Ni-based Alloy Composite Coating by Laser Cladding
董刚
严彪
Journal of Wuhan University of Technology(Materials Science), 2012, (02) : 231 - 237

← 1 2 3 4 5 →