Thermoelectric properties of the β-cu2se films with ag doping by magnetron sputtering

被引：0
|
作者：
Li G.-P. [1 ]
Song G.-H. [1 ]
Wang N. [1 ]
Li X.-Y. [1 ]
Hu F. [1 ]
机构：
[1] School of Materials Science and Engineering, Shenyang University of Technology, Shenyang
来源：
Surface Technology | 2021年 / 50卷 / 08期
基金：
中国国家自然科学基金;
关键词：
Ag doping; Cu2Se films; Magnetron sputtering; Resistivity; Seebeck coefficient; Thermoelectric materials;
D O I：
10.16490/j.cnki.issn.1001-3660.2021.08.020
中图分类号：
学科分类号：
摘要：
The work aims to study the influence of Ag doping on the phase composition and thermoelectric properties of Cu2Se thin films. Ag-doped Cu2Se thermoelectric thin films were deposited by high vacuum magnetron sputtering using a powder sintered Cu2Se alloy target. The influence of Ag doping on the phase composition and thermoelectric properties of the Cu2Se thin films were studied in this paper. The phase composition, surface morphologies, fracture cross-sections, micro-area element contents and element distribution of the thin films were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS). The thermoelectric properties of the Cu2Se films with different Ag contents were studied by measuring the resistivity and Seebeck coefficient by Seebeck coefficient/resistance analysis system LSR-3. The results show that the use of magnetron sputtering technology and α-Cu2Se alloy target can prepare Cu-Se thin films with β-Cu2Se phase as the main phase and a very small amount of α-Cu2Se phase. The Ag atom doped in the films does not enter the lattice of the β-Cu2Se phase, but forms a nano-sized CuAgSe second phase in the films. The β-Cu2Se phase lattice of the deposited films is rich in Cu. When the Ag content increases from 0 to 2.97at%, the ratio of [Cu]/[Se] in the β-Cu2Se phase lattice is more than the ideal ratio of 2.0, enhancing from 3.59 to 4.96.The resistivity of the deposited β-Cu2Se films is significantly lower than that of bulk materials in the literature due to Cu-rich in β-Cu2Se phase lattice. With the increase of Ag content, the resistivity of the deposited β-Cu2Se films decreases first and then increases, the Seebeck coefficient of the films increases with resistivity. The sample with Ag content of 1.37at% has the highest power factor due to the significantly higher Seebeck coefficient. The Cu-rich β-Cu2Se films prepared by magnetron sputtering has low resistivity, and the appropriate amount of Ag-doping can significantly increase the absolute value of the Seebeck coefficient, thereby obtaining a higher power factor. © 2021, Chongqing Wujiu Periodicals Press. All rights reserved.
引用
收藏
页码：218 / 226
页数：8
相关论文
共 37 条
  • [31] Feng J., Phase Selective Synthesis of Cu2se and Mechanism Study of the α-Cu2Se/β-Cu2Se Phase Transition[D], (2015)
  • [32] Tak J.Y., Nam W.H., Lee C., Et al., Ultralow lattice thermal conductivity and significantly enhanced nearroom-temperature thermoelectric figure of merit in α-Cu2Se hrough suppressed Cu vacancy formation by overstoichiometric Cu addition[J], Chemistry of Materials, 30, 10, pp. 3276-3284, (2018)
  • [33] Bhardwaj R., Bhattacharya A., Tyagi K., Et al., Enhancement in thermoelectric performance of single step synthesized Mg doped Cu2Se: An experimental and theoretical study[J], Intermetallics, 112, (2019)
  • [34] Jing-Yi W., Bin L.I.U., Nai-Hua M., Et al., I-doped Cu2Se nanocrystals for high-performance thermoelectric applications[J], Journal of Alloys and Compounds, 772, pp. 366-370, (2019)
  • [35] Ghosh A., Kulsi C., Banerjee D., Et al., Galvanic synthesis of Cu2−XSe thin films and their photocatalytic and thermoelectric properties[J], Applied Surface Science, 369, pp. 525-534, (2016)
  • [36] Yao L.U., Yu-Fei D.I.N.G., Yang Q., Et al., Good performance and flexible PEDOT: PSS/Cu2Se nanowire thermoelectric composite films[J], ACS Applied Materials & Interfaces, 11, 13, pp. 12819-12829, (2019)
  • [37] Snyder G.J., Toberer E.S., Complex thermoelectric materials[J], Nature Materials, 7, 2, pp. 105-114, (2008)
1234