Abrasion Resistance Mechanism of New Co-Based Alloy by Diode Laser Cladding

被引：0
|
作者：
Wu G. [1 ,2 ]
Ren F. [1 ,2 ]
Yao J. [1 ,2 ]
Mao W. [3 ]
Li H. [3 ]
机构：
[1] Institute of Laser Advanced Manufacturing, Zhejiang University of Technology, Hangzhou, 310014, Zhejiang
[2] Zhejiang Provincial Collaborative Innovation Center of High-end Laser Manufacturing Equipment, Hangzhou, 310014, Zhejiang
[3] Bray (China) Controls System Co. Ltd, Hangzhou, 311231, Zhejiang
来源：
Yao, Jianhua (laser@zjut.edu.cn) | 1600年 / Science Press卷 / 44期
关键词：
Abrasion resistance; Co-based alloy; Laser cladding; Laser technique; Microstructure;
D O I：
10.3788/CJL201744.0602006
中图分类号：
学科分类号：
摘要：
Stellite 3, Stellite 21 and new Co-based alloy (Co-3) coatings are prepared on the 316 stainless steel surface by laser cladding. The microstructure and phase composition of the cladding layers are analysed and the microhardness distribution and abrasion resistance mechanism are also studied. The experimental results show that the microstructure of the Co-3 is homogeneous, compact, and without cracks and cavity, where the main phases consist of (Co,W)3C, Cr23C6, Cr7C3, and Co3Mo. The average microhardness of the cladding layer is about 624 HV0.2, which is more than 3 times higher than that of the substrate. The abrasion resistance performance of Co-3 is superior to that of the 316 substrate. Under the load of 0~150 N condition, when the scratching length s≤3.3 mm, the main scratch mechanism is plastic deformation; when the scratching length 3.3<s≤6.9 mm, the main scratch mechanism is grain sliding and crack formation caused by plastic deformation; when the scratching length s>6.9 mm, the main scratch mechanism is crack propagation and plastic removal. © 2017, Chinese Lasers Press. All right reserved.
引用
下载
收藏
相关论文
共 16 条
  • [1] Lu S., Introduction to Stainless Steel, pp. 80-89, (2013)
  • [2] Lin H., Wang J., Application and improvement of wear resistant valve in coal liquefaction equipment, Universal Machine, 8, pp. 36-38, (2012)
  • [3] Gao Q., Valve Surfacing Technology, pp. 37-42, (1994)
  • [4] Lin H., Requirements of modern coal-to-chemicals to wear-resistance valve, Fluid Machinery, 41, 7, pp. 49-52, (2013)
  • [5] Yao J., Li C., Research and application of laser surface strengthening and remanufacturing technology, Electric Welding Machine, 42, 5, pp. 15-19, (2012)
  • [6] Xu G.J., Kutsuna M., Liu Z.J., Comparison between diode laser and TIG cladding of Co-based alloys on the SU403 stainless steel, Surface and Coating Technology, 201, 3-4, pp. 1138-1144, (2006)
  • [7] Zhang X., Dong S., Xu B., Et al., Microstructure and impact abrasive wear resistance of the St6 cobalt-based alloy laser cladding layer, Applied Laser, 31, 1, pp. 82-85, (2011)
  • [8] Li C., Liu H., Zhang X., Et al., Microstructure and property of Co-based carbide composite coating fabricated by laser cladding on 40Cr tool steel surface, Chinese J Lasers, 42, 11, (2015)
  • [9] Li Z., Yang L., Li B., Et al., Microstructural characteristics of WC/Stellite 6 composite coating prepared by supersonic laser deposition, Chinese J Lasers, 42, 11, (2015)
  • [10] Kapoor S., Liu R., Wu X.J., Et al., Microstructure and wear resistance relations of Stellite alloys, International Journal of Advanced Materials Sciences, 4, 3, pp. 231-248, (2013)
12