Acoustic emission during fracture of ceramic superconducting materials

被引：0
|
作者：
机构：
[1] Woźny, L.
[2] Kisiel, A.
[3] Lysy, K.
来源：
| 1600年 / IOP Publishing Ltd卷 / 113期
关键词：
In the ceramic materials acoustic emission (AE) is associated with a rapid elastic energy release due to the formation and expansion of cracks; which causes generation and propagation of the elastic wave. AE pulses measurement allows monitoring of internal stresses changes and the development of macro- and micro-cracks in ceramic materials; and that in turn allows us to evaluate the time to failure of the object. In presented work the acoustic signals generated during cracking of superconducting ceramics were recorded. Results obtained were compared with other ceramic materials tested the same way. An analysis of the signals was carried out. The characteristics of the AE before destruction of the sample were determined; that allow the assessment of the condition of the material during operation and its expected lifetime. © Published under licence by IOP Publishing Ltd;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
相关论文
共 50 条
  • [1] ANOMALIES OF ACOUSTIC-EMISSION IN CERAMIC MATERIALS DURING FATIGUE TESTS
    BARANOV, VM
    DOBROVOLSKII, IO
    [J]. SOVIET JOURNAL OF NONDESTRUCTIVE TESTING-USSR, 1984, 20 (07): : 476 - 478
  • [2] ACOUSTIC-EMISSION AND FRACTURE OF DUCTILE MATERIALS
    MASOUNAVE, J
    LANTEIGNE, J
    BASSIM, MN
    HAY, DR
    [J]. ENGINEERING FRACTURE MECHANICS, 1976, 8 (04) : 701 - &
  • [3] Acoustic emission studies during indentation on ceramic and ceramic composite
    Ray, AK
    Bhattacharya, DK
    Das, G
    [J]. TRENDS IN NDE SCIENCE AND TECHNOLOGY - PROCEEDINGS OF THE 14TH WORLD CONFERENCE ON NDT (14TH WCNDT), VOLS 1-5, 1996, : 2455 - 2458
  • [4] The Acoustic Emission Method Application for Producing a Growing Sharp Crack and Evaluation of the Fracture Toughness of Ceramic Materials
    Drozdov, A. V.
    [J]. STRENGTH OF MATERIALS, 2013, 45 (03) : 301 - 307
  • [5] INVESTIGATION OF THE BRITTLE-FRACTURE OF CERAMIC MATERIALS USING MICROCOMPUTER PROCESSING OF ACOUSTIC-EMISSION SIGNALS
    RANACHOWSKI, J
    REJMUND, F
    MIKIEL, W
    RANACHOWSKI, Z
    [J]. ULTRASONICS, 1987, 25 (06) : 374 - 374
  • [6] The Acoustic Emission Method Application for Producing a Growing Sharp Crack and Evaluation of the Fracture Toughness of Ceramic Materials
    A. V. Drozdov
    [J]. Strength of Materials, 2013, 45 : 301 - 307
  • [7] Evaluation of fracture behavior in metal/ceramic joint by acoustic emission
    Park, YJ
    Enoki, M
    Suga, T
    Kishi, T
    [J]. NONDESTRUCTIVE CHARACTERIZATION OF MATERIALS IX, 1999, 497 : 21 - 26
  • [8] Acoustic emission technique for fracture analysis in wood materials
    Lamy, Frederic
    Takarli, Mokhfi
    Angellier, Nicolas
    Dubois, Frederic
    Pop, Octavian
    [J]. INTERNATIONAL JOURNAL OF FRACTURE, 2015, 192 (01) : 57 - 70
  • [9] Acoustic emission technique for fracture analysis in wood materials
    Frédéric Lamy
    Mokhfi Takarli
    Nicolas Angellier
    Frédéric Dubois
    Octavian Pop
    [J]. International Journal of Fracture, 2015, 192 : 57 - 70
  • [10] Disintegration and fracture of heterogeneous materials related to acoustic emission
    Gorobets, LZ
    Shulyak, IA
    Verkhorobina, IV
    [J]. REFRACTORIES AND INDUSTRIAL CERAMICS, 2004, 45 (03) : 220 - 221
12345