Preparation and properties of Yb2O3-Y2O3- Gd2O3-ZrO2 ceramics for thermal barrier coatings

被引：0

作者：

Sun, Xian-Kai ^{[1
]}

Wang, Quan-Sheng ^{[1
]}

Liu, Yan-Bo ^{[1
]}

Du, Zhong ^{[1
]}

Zhang, Rui ^{[1
]}

机构：

[1] National Key Laboratory of Science and Technology on Materials under Shock and Impact, School of Materials Science and Engineering, Beijing Institute of Technology, Beijing 100081, China

来源：

Rengong Jingti Xuebao/Journal of Synthetic Crystals | 2013年 / 42卷 / 06期

关键词：

Ceramic materials - Particle size - Thermal barrier coatings - Gadolinium compounds - Plasma jets - Chlorine compounds - Powders - Zirconia - Coprecipitation - Plasma spraying - Sintering - Sprayed coatings - X ray diffraction;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Yb2O3-Y2O3- Gd2O3-ZrO2 (YYGZO) composition powder was synthesized by the chemical coprecipitation method using Yb2O3, Y2O3, Gd2O3 and ZrOCl2&middot 8H2O powders as raw materials, and applied as ceramic topcoats of thermal barrier coating (TBC) by atmospheric plasma spraying (APS). Microstructure and phases of YYGZO powder and thermal barrier coatings were examined by scanning electrical microscopy (FESEM) and X-ray diffraction (XRD). The results showed that the YYGZO ceramics powder were prepared with solid sphere shape and proper distribution of particle size about 30-60 μm by spray-dried method are suitable for atmospheric plasma spraying. Phase analyses revealed that YYGZO coatings keep the single phase before and after under heat treatment at 1200°C. The coating has compact microstructure and higher binging strength between the topcoat and bondcoat. The bingding strength and porosity of the coating are about 35.2 MPa and 9.23%, respectively.

引用

页码：1213 / 1216

共 50 条

[21] Preparation of Al2O3-ZrO2-Y2O3 Composite Coatings by a Modified Sol-Gel Technique for Thermal Barrier Application
Zhang, Kun
Liu, Li
Ren, Chao
Wang, Kai
Dai, Guangze
Zheng, Xuebin
He, Yedong
OXIDATION OF METALS, 2013, 80 (3-4): : 323 - 339
[22] Investigation of the Physicochemical Properties of Ceramics in the Sm2O3-Y2O3-HfO2System for Developing Promising Thermal Barrier Coatings
Kablov, E. N.
Doronin, O. N.
Artemenko, N. I.
Stekhov, P. A.
Marakhovskii, P. S.
Stolyarova, V. L.
RUSSIAN JOURNAL OF INORGANIC CHEMISTRY, 2020, 65 (06) : 914 - 923
[23] Phase stability and thermal conductivity of RE2O3 (RE = La, Nd, Gd, Yb) and Yb2O3 co-doped Y2O3 stabilized ZrO2 ceramics
Guo, Lei
Li, Mingzhu
Ye, Fuxing
CERAMICS INTERNATIONAL, 2016, 42 (06) : 7360 - 7365
[24] Microstructure of sintered ZrO2-Al2O3-Y2O3 ceramics
Antsiferov, VN
Peshcherenko, SN
Sevast'yanova, IG
INORGANIC MATERIALS, 1997, 33 (12) : 1299 - 1302
[25] Microstructure of Sintered ZrO2-Al2O3-Y2O3 Ceramics
Antsiferov, V. N.
Peshcherenko, S. N.
Sevast'yanova, I. G.
Inorganic Materials, 33 (12):
[26] y ZrO2-Sc2O3 Solid Electrolytes Doped with Yb2O3 or Y2O3
Lomonova, E. E.
Agarkov, D. A.
Borik, M. A.
Eliseeva, G. M.
Kulebyakin, A. V.
Kuritsyna, I. E.
Milovich, F. O.
Myzina, V. A.
Osiko, V. V.
Chislov, A. S.
Tabachkova, N. Yu.
RUSSIAN JOURNAL OF ELECTROCHEMISTRY, 2020, 56 (02) : 118 - 123
[27] Yb2O3-Gd2O3codoped strontium zirconate composite ceramics for potential thermal barrier coating applications
Zhang, Jingxin
Bai, Yu
Li, Enbo
Dong, Hongying
Ma, Wen
INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2020, 17 (04) : 1608 - 1618
[28] Toughening effect of Yb2O3 stabilized ZrO2 doped in Gd2Zr2O7 ceramic for thermal barrier coatings
Zhang, Yu
Guo, Lei
Zhao, Xiaoxiang
Wang, Caimei
Ye, Fuxing
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 648 : 385 - 391
[29] Improvement on the phase stability, mechanical properties and thermal insulation of Y2O3-stabilized ZrO2 by Gd2O3 and Yb2O3 co-doping
Guo, Lei
Guo, Hongbo
Gong, Shengkai
Xu, Huibin
CERAMICS INTERNATIONAL, 2013, 39 (08) : 9009 - 9015
[30] Gd2O3-Yb2O3-Y2O3-ZrO2热障涂层材料的热物理性能
李嘉
谢铮
何箐
邹晗
吕玉芬
表面技术, 2015, 44 (09) : 18 - 22+42

← 1 2 3 4 5 →