The interaction between diamond like carbon (DLC) coatings and ionic liquids under boundary lubrication conditions

被引：0
|
作者：
机构：
[1] Milewski, K.
[2] Kudliński, J.
[3] Madej, M.
[4] Ozimina, D.
来源：
| 1600年 / Faculty of Metallurgy卷 / 56期
关键词：
Tribology - Carbon - Scanning electron microscopy - Surface topography - Ionic liquids - Physical vapor deposition - Coatings;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The aim of the study was to analyse antiwear DLC coatings produced by physical vapour deposition. The a-C:H coatings were deposited on steel elements designed to operate under friction conditions. The coating structure was studied by observing the surface topography with a scanning electron microscope (SEM) and a profilometer. The friction and wear properties of the coatings were examined using a ball-on-disc tribotester. The lubricants tested were two types of ionic liquids (1-butyl-3-methylimidazolium tetrafluoroborate and trihexyltetradecylphosphonium bis(trifluoromethy-lsulphonyl) amide). The experimental data was used to select ionic liquids with the best tribological properties to operate under lubricated friction conditions and interact with DLC coatings. © 2017, Faculty of Metallurgy. All rights reserved.
引用
收藏
页码：1 / 2
相关论文
共 50 条
  • [21] Scratch resistance and tribological properties of DLC coatings under dry and lubrication conditions
    Sharma, Neha
    Kumar, N.
    Dash, S.
    Das, C. R.
    Rao, R. V. Subba
    Tyagi, A. K.
    Raj, Baldev
    TRIBOLOGY INTERNATIONAL, 2012, 56 : 129 - 140
  • [22] Surface damage and wear mechanisms of amorphous carbon coatings under boundary lubrication conditions
    Ajayi, OO
    Kovalchenko, A
    Hersberger, JG
    Erdemir, A
    Fenske, GR
    SURFACE ENGINEERING, 2003, 19 (06) : 447 - 453
  • [23] Lubrication performance of diamond-like carbon and fluorinated diamond-like carbon coatings for intravascular guidewires
    Hasebe, T
    Matsuoka, Y
    Kodama, H
    Saito, T
    Yohena, S
    Kamijo, A
    Shiraga, N
    Higuchi, A
    Kuribayashi, S
    Takahashi, K
    Suzuki, T
    DIAMOND AND RELATED MATERIALS, 2006, 15 (01) : 129 - 132
  • [24] Tribological Behavior of Diamond-like Carbon Coatings under Boundary Friction: Part II. Lubrication with Chemically Modified Layers
    I. A. Buyanovskii
    M. M. Khrushchov
    V. D. Samusenko
    Inorganic Materials: Applied Research, 2022, 13 : 907 - 913
  • [25] Tribological Behavior of Diamond-like Carbon Coatings under Boundary Friction: Part II. Lubrication with Chemically Modified Layers
    Buyanovskii, I. A.
    Khrushchov, M. M.
    Samusenko, V. D.
    INORGANIC MATERIALS-APPLIED RESEARCH, 2022, 13 (04) : 907 - 913
  • [26] THE EFFECT OF MOLYBDENUM TRIOXIDE ON WEAR OF DIAMOND-LIKE CARBON UNDER BOUNDARY LUBRICATION CONDITION
    Tokoroyama, Takayuki
    Nishino, Takahiro
    IRF2016: 5TH INTERNATIONAL CONFERENCE INTEGRITY-RELIABILITY-FAILURE, 2016, : 339 - 348
  • [27] The Lubrication Properties of Diamond-like Carbon Coatings in Engine Oil
    Nie, Chaoyin
    Liu, Xiaokui
    Watanabe, Hisashi
    MATERIALS RESEARCH, PTS 1 AND 2, 2009, 610-613 : 652 - 657
  • [28] Tribological characteristics of diamond-like carbon (DLC) based nanocomposite coatings
    Wu, JH
    Karthikeyan, S
    Falk, ML
    Rigney, DA
    WEAR, 2005, 259 (1-6) : 744 - 751
  • [29] Advances in multi-spectral Diamond-Like Carbon (DLC) coatings
    Keck, Jason
    Karp, Christopher
    WINDOW AND DOME TECHNOLOGIES AND MATERIALS XIV, 2015, 9453
  • [30] THE PROPERTIES OF DIAMOND - LIKE CARBON (DLC) COATINGS ON TITANIUM ALLOYS FOR BIOMEDICAL APPLICATIONS
    Madej, M.
    METALURGIJA, 2022, 61 (3-4): : 669 - 672
12345