Unveiling the mechanism of yttrium-related microstructure inhibiting or promoting high-temperature oxidation based on Ni-Al-Y alloys

被引：0
|
作者：
Wu, Yun [1 ,2 ]
Li, Yunting [3 ]
Xu, Yuantao [2 ,4 ]
Kang, Maodong [1 ,2 ]
Wang, Jun [1 ,2 ]
Sun, Baode [1 ,2 ]
机构：
[1] Shanghai Key Laboratory of Advanced High-temperature Materials and Precision Forming, Shanghai Jiao Tong University, Shanghai,200240, China
[2] School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai,200240, China
[3] Instrumental Analysis Center, Shanghai Jiao Tong University, Shanghai,200240, China
[4] Shanghai Key Laboratory of Materials Laser Processing and Modification, Shanghai Jiao Tong University, Shanghai,200240, China
来源：
Acta Materialia | 2021年 / 211卷
关键词：
This work was financially supported by the National Natural Science Foundation of China (No. 51971142; 52031012; National Science and Technology Major Project of China (No. 2017 - Ⅵ - 0013 - 0085 ); Aeronautical Science Foundation of China (No. 2018ZE57012 ); and Startup Fund for Youngman Research at SJTU (No. 18×100040027). B.S. would like to acknowledge the technical support from Instrumental Analysis Center; Shanghai Jiao Tong University. Y.W. would like to acknowledge the software support from Oxford Instruments NanoAnalysis;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
62
引用
收藏
相关论文
共 50 条
  • [11] EFFECT OF YTTRIUM ADDITION ON THE HIGH-TEMPERATURE OXIDATION RESISTANCE OF NI3AL ALLOY
    OCHIAI, S
    SUZUKI, T
    KOJIMA, Y
    KOBAYASHI, M
    TORISAKA, Y
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1989, 53 (06) : 585 - 592
  • [12] High-temperature oxidation behavior of as-cast Ni-Cr-Al-Fe based alloys
    Han, Chao
    Liu, Yong
    Wang, Yan
    Li, Wei-Jie
    Tang, Hui-Ping
    Fenmo Yejin Cailiao Kexue yu Gongcheng/Materials Science and Engineering of Powder Metallurgy, 2011, 16 (06): : 806 - 814
  • [13] Microstructure and Oxidation Resistance of Cr-Al-Si Alloys for High-Temperature Applications
    Kim, Jeong-Min
    Kim, Chae-Young
    COATINGS, 2020, 10 (04)
  • [14] Effect of Si content on the surface high-temperature oxidation mechanism in Ni5Y-containing NiAIYSi alloys
    Wang, Fangming
    Zhou, Ruonan
    Xu, Kai
    Lou, Ming
    Chang, Keke
    CORROSION SCIENCE, 2023, 218
  • [15] HIGH-TEMPERATURE OXIDATION BEHAVIOR OF A NI-CR-AL-FE-Y ALLOY
    TAWANCY, HM
    SRIDHAR, N
    OXIDATION OF METALS, 1992, 37 (3-4): : 143 - 166
  • [16] HIGH-TEMPERATURE OXIDATION RESISTANCE OF ALLOYS OF THE NI3TI-NI3AL SYSTEM
    LARIKOV, LN
    OMELYANENKO, VV
    TYSHKEVICH, VM
    PROTECTION OF METALS, 1983, 19 (01): : 122 - 124
  • [17] MECHANISMS OF ADHERENCE OF ALUMINA SCALE DEVELOPED DURING HIGH-TEMPERATURE OXIDATION OF FE-NI-CR-AL-Y ALLOYS
    DELAUNAY, D
    HUNTZ, AM
    JOURNAL OF MATERIALS SCIENCE, 1982, 17 (07) : 2027 - 2036
  • [18] Evolution of Bimodal Microstructure and High-Temperature Wear Resistance of Al-Cu-Ni Alloys
    Maity, Shubhadeep
    Chanda, Dipak Kr
    Ramasamy, Parthiban
    Show, Bijay Kumar
    Eckert, Juergen
    Bera, Supriya
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2020, 51 (01): : 109 - 115
  • [19] Evolution of Bimodal Microstructure and High-Temperature Wear Resistance of Al-Cu-Ni Alloys
    Shubhadeep Maity
    Dipak Kr. Chanda
    Parthiban Ramasamy
    Bijay Kumar Show
    Jürgen Eckert
    Supriya Bera
    Metallurgical and Materials Transactions A, 2020, 51 : 109 - 115
  • [20] On the Role of Yttrium in Alumina Formers: Comparative Oxidation Behavior of (Ni-Cr-Al)- and (Ni-Cr-Al-Y)-Based Alloys
    Tawancy, H. M.
    OXIDATION OF METALS, 2016, 86 (3-4): : 371 - 383
12345