Effect of Self-lubricating Organic Silicone Component on Antifouling and Drag Reduction Properties of Self-polishing Coatings

被引：0
|
作者：
Zhang J.-B. [1 ,2 ]
Zhang C.-Y. [1 ]
Sun L. [3 ]
Yu B. [1 ]
Yang W.-F. [1 ,4 ]
Pei X.-W. [1 ]
Zhou F. [1 ]
机构：
[1] Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou
[2] University of Chinese Academy of Sciences, Beijing
[3] State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou
[4] Yantai Zhongke Research Institute of Advanced Materials and Green Chemical Engineering, Shandong, Yantai
来源：
Surface Technology | 2022年 / 51卷 / 05期
基金：
中国国家自然科学基金;
关键词：
drag reduction; environmentally friendly; fouling release; marine antifouling; self-lubricating; silicone coating;
D O I：
10.16490/j.cnki.issn.1001-3660.2022.05.028
中图分类号：
学科分类号：
摘要：
To prepare an environment-friendly protective coating with marine antifouling and drag reduction functions, a novel long-chain linear silicone molecules were intelligently integrated in polymer resin, and the self-lubricating coating was prepared compounded with certain inorganic pigment. Foundational properties of coating, including hardness, impact resistance, adhesion, viscoelasticity, surface roughness, surface wettability and self-lubricating properties, were evaluated respectively. Moreover, the antifouling performance of the coating was characterized in terms of different fouling scales, from protein, algae to marine organism, and the drag reduction property of the coating was also measured by a rheometer. The results indicated that the coating hardness descended from 2H to 4B, the adhesion grade changed from 0 grade to 2 grade and the impact resistance decreased slightly with the increase of self-lubricating organic silicone component in the coating, while the contact angle increased from 65° to 92°. Importantly, the self-lubricating properties, antifouling and drag reduction performance of the coating were significantly enhanced with the increase of organic silicon monomer, which were attributed to the minimal surface roughness (less than 500 nm). The friction coefficient under the dry grinding condition was also expected to decreased from 0.119 to 0.075. Besides, when the mass content of organic silicon component was more than 20%, the 97% antifouling ratio of marine algae and 10% drag reduction efficiency were achieved. Finally, the marine field test further proved the excellent antifouling and comprehensive performance of the coating. This research provided a method of preparing silicon coating with both antifouling and drag reduction functions through chemically integrating linear long-chain silicone component in the coating binding resin. Giving their environmental-friendly character, stable performances and facile preparation method, the as-prepared coating had a bright application prospect in the field of marine equipment protection. © 2022, Chongqing Wujiu Periodicals Press. All rights reserved.
引用
收藏
页码：274 / 282
页数：8
相关论文
共 27 条
  • [21] ZHOU Jia-jun, LI Xue-ling, LI Xia, Et al., Progress in Silicone-Modified Environmental Friendly Marine Anti-fouling Coatings, Paint & Coatings Industry, 46, 6, pp. 75-80, (2016)
  • [22] MAO Shi-hua, ZHANG Dong, HE Xiao-min, Et al., Mussel-Inspired Polymeric Coatings to Realize Functions from Single and Dual to Multiple Antimicrobial Mechani-sms, ACS Applied Materials & Interfaces, 13, 2, pp. 3089-3097, (2021)
  • [23] JIA Ning, DAI Shuai-shuai, HE Guang-ling, Et al., Characterization Method of Hydrogel Antifouling Materials, Paint & Coatings Industry, 51, 9, pp. 74-80, (2021)
  • [24] ZHANG Wen-yu, Advances in the Study of Microbiolo-gically Influenced Corrosion in Marine Environment, Total Corrosion Control, 31, 1, pp. 8-12, (2017)
  • [25] SELIM M S, SHENASHEN M A, EL-SAFTY S A, Et al., Recent Progress in Marine Foul-Release Polymeric Nano-composite Coatings, Progress in Materials Science, 87, pp. 1-32, (2017)
  • [26] QIN Li-guo, YANG Hao, DONG Guang-neng, Et al., Application of Textured Surface Flexible Materials in Drag Reduction and Antifouling of Marine Equipment, Surface Technology, 48, 6, pp. 150-157, (2019)
  • [27] SUN Wei-hong, LIU Bo, YAN Xin, Drag Reduction Properties of Polyurethane-Poly(Acrylate) Hybrid Emul-sions, Polymer Materials Science & Engineering, 33, 9, pp. 59-64, (2017)
123