Influence of corrosion processes on friction and wear of tin coatings of wire connectors

被引：0
|
作者：
GRYGIER D. [1 ]
KOWALEWSKI P. [2 ]
RADZINSKA A. [3 ]
机构：
[1] Wroclaw University of Science and Technology, Faculty of Mechanical Engineering, Department of Vehicle Engineering, Wybrzeze Wyspianskiego 27, Wroclaw
[2] Wroclaw University of Science and Technology, Faculty of Mechanical Engineering, Department of Machine Design and Mechatronic Systems, Wybrzeze Wyspianskiego 27, Wroclaw
[3] Wroclaw University of Science and Technology, Wybrzeze Wyspianskiego 27, Wroclaw
来源：
Tribologia | 2020年 / 294卷 / 06期
关键词：
Connectors; Corrosion; Electrical connectors; Tin coatings;
D O I：
10.5604/01.3001.0014.8331
中图分类号：
学科分类号：
摘要：
The paper describes the results of metallographic, tribological, and microscopic tests of wire connectors. It was shown that the structure and thickness of the tin layer on the copper element varies greatly. The paper describes the results of tribological investigations for electrical connectors in the initial state and covered with a layer of oxides formed as a result of corrosion. The results of tribological tests have shown a great influence of the oxide layer on friction and wear of tin coatings. The results of friction factor measurements were confirmed by microscopic observations. The tests confirmed that the oxide layer reduces plastic deformation of the tin coating and limits its tribological wear. Due to the brittleness and low adhesion of the oxide layer, friction-induced chipping was observed. © 2020 Helsinki University of Technology. All rights reserved.