Analytical-Experimental Evaluation of the Fatigue Resistance for Aircraft Fuselage Skin in the Case of Corrosion Damage

被引：0
|
作者：
Shapkin, V.S. [1 ]
Lapaev, A.V. [2 ]
Matveev, K.A. [3 ]
Gorshkov, V.A. [4 ]
Bogoyavlenskii, A.A. [4 ]
机构：
[1] National Research Center Zhukovsky Institute, ul. Viktorenko 7, Moscow,125319, Russia
[2] LLC West Siberian Center for Certification of Air Transport Facilities, ul. Novaya Zarya 2a, Novosibirsk,630084, Russia
[3] Novosibirsk State Technical University, prospekt K. Marksa 20, Novosibirsk,630073, Russia
[4] State Research Institute of Civil Aviation, ul. Mikhalkovskaya 67, str. 1, Moscow,125438, Russia
来源：
Russian Aeronautics | 2021年 / 64卷 / 02期
关键词：
Airframes;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：181 / 188
相关论文
共 50 条
  • [41] EXPERIMENTAL EVALUATION OF THE RESISTANCE OF THE SKIN GRAFTED RECTUM TO ILEAL CONTENTS
    HARRISON, RC
    OKA, H
    OWEN, DA
    AMERICAN JOURNAL OF SURGERY, 1984, 147 (05): : 624 - 628
  • [42] Rosette eddy current sensor and its experimental research on aircraft metallic structure fatigue damage monitoring
    Ding, Hua
    He, Yuting
    Du, Jinqiang
    Jiao, Shenbo
    Jixie Gongcheng Xuebao/Journal of Mechanical Engineering, 2013, 49 (02): : 1 - 7
  • [43] Evaluation of Fatigue Cracking Resistance of Asphalt Mixtures Using Apparent Damage Capacity
    Etheridge, Robert Austin
    Wang, Yizhuang David
    Kim, S. Sonny
    Kim, Y. Richard
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2019, 31 (11)
  • [44] Fatigue crack growth from corrosion damage in 7075-T6511 aluminium alloy under aircraft loading
    DuQuesnay, DL
    Underhill, PR
    Britt, HJ
    INTERNATIONAL JOURNAL OF FATIGUE, 2003, 25 (05) : 371 - 377
  • [45] EXPERIMENTAL EVALUATION OF CONDUCTOR AEOLIAN FATIGUE DAMAGE MITIGATION BY AMPLITUDE REDUCTION.
    Ramey, George E.
    Silva, J.Mike
    SAE Preprints, 1981,
  • [46] An experimental approach for non-destructive evaluation of fatigue damage in CFRP composites
    Bhat, MR
    Murthy, CRL
    TRENDS IN NDE SCIENCE AND TECHNOLOGY - PROCEEDINGS OF THE 14TH WORLD CONFERENCE ON NDT (14TH WCNDT), VOLS 1-5, 1996, : 2529 - 2532
  • [47] Estimation of corrosion fatigue life by evaluation on corrosion pit damage in gas turbine compressor blades under service conditions
    Hitachi Works, Hitachi Ltd., Saiwai-Cho, Hitachi, 317-8511, Japan
    不详
    不详
    Zairyo, 2013, 6 (383-389):
  • [48] Effect of different types of calcined crude kaolins and high purity metakaolin on corrosion resistance of reinforcement in concretes: Experimental evaluation and analytical modeling
    Mermerdas, Kasim
    Guneyisi, Erhan
    CONSTRUCTION AND BUILDING MATERIALS, 2023, 382
  • [49] Post-failure life evaluation: A corrosion-fatigue case history
    Diaz, E.
    Soria, L.
    Gallardo, J. M.
    ENGINEERING FAILURE ANALYSIS, 2019, 105 : 828 - 836
  • [50] EVALUATION OF SKIN DAMAGE .1. SKIN RESISTANCE MEASUREMENTS WITH ALTERNATING-CURRENT (IMPEDANCE MEASUREMENTS)
    THIELE, FAJ
    MALTEN, KE
    BRITISH JOURNAL OF DERMATOLOGY, 1973, 89 (04) : 373 - 382
12345