Effect of alternating current and nitrate reducing bacteria on corrosion of X80 pipeline steel in Shenyang soil solution

被引：0
|
作者：
Fu, Qi [1 ,2 ]
Xu, Jin [2 ,3 ]
Wei, Boxin [1 ,2 ]
Qin, Qingyu [1 ,2 ]
Gao, Liqun [2 ]
Bai, Yunlong [2 ,3 ]
Yu, Changkun [2 ,3 ]
Sun, Cheng [2 ,3 ]
机构：
[1] School of Materials Science and Engineering, University of Science and Technology of China, Shenyang,110016, China
[2] Institute of Metal Research, Chinese Academy of Sciences, Shenyang,110016, China
[3] Liaoning Shenyang Soil and Atmosphere Corrosion of Material National Observation and Research Station, Shenyang,110016, China
来源：
Engineering Failure Analysis | 2021年 / 129卷
基金：
中国国家自然科学基金;
关键词：
Steel corrosion - Soil moisture - Bacteria - Nitrates - Surface analysis - Corrosive effects - Steel pipe - Underground corrosion - Pitting - Pipeline corrosion - Pipelines;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
相关论文
共 50 条
  • [41] Effect of uniaxial elastic stress on corrosion of X80 pipeline steel in an acidic soil solution containing sulfate-reducing bacteria trapped under disbonded coating
    Wei, Boxin
    Xu, Jin
    Cheng, Y. Frank
    Sun, Cheng
    Yu, Changkun
    Wang, Zhenyao
    CORROSION SCIENCE, 2021, 193
  • [42] Effects of alternating current on microbiologically synergistic corrosion of pipeline steel X80 applied by elastic stress
    Zheng Cai
    Qingyu Qin
    Ying Liu
    Boxin Wei
    Naiyan Zhang
    Jin Xu
    Qi Fu
    Changkun Yu
    Cheng Sun
    Corrosion Communications, 2024, 13 (01) : 1 - 16
  • [43] Synergistic effect of sulphate-reducing bacteria and external tensile stress on the corrosion behaviour of X80 pipeline steel in neutral soil environment
    Xie, Fei
    Li, Xue
    Wang, Dan
    Wu, Ming
    Sun, Dongxu
    ENGINEERING FAILURE ANALYSIS, 2018, 91 : 382 - 396
  • [44] Hydrogen permeation in X80 steel during corrosion induced by the synergistic effects of sulfate-reducing bacteria and alternating current
    Yan, Mengdi
    Wei, Boxin
    Xu, Jin
    Yu, Changkun
    Sun, Cheng
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2025, 106 : 604 - 615
  • [45] Effect of residual and external stress on corrosion behaviour of X80 pipeline steel in sulphate-reducing bacteria environment
    Li, Xue
    Xie, Fei
    Wang, Dan
    Xu, Changhao
    Wu, Ming
    Sun, Dongxu
    Qi, Jianjing
    ENGINEERING FAILURE ANALYSIS, 2018, 91 : 275 - 290
  • [46] Effect of applied potentials on stress corrosion cracking susceptibility of X80 pipeline steel in simulated soil solution
    Cheng, Yuan
    Yu, Hongying
    Zhang, Lixin
    Wang, Ying
    Meng, Xu
    Sun, Dongbai
    ADVANCES IN SUPERALLOYS, PTS 1 AND 2, 2011, 146-147 : 920 - +
  • [47] Effect of cathode potentials on stress corrosion behavior of X80 pipeline steel in simulated alkaline soil solution
    Wang, Dan
    Xie, Fei
    Wu, Ming
    Chen, Xu
    Fu, Yang
    Zhang, Wenjian
    Ge, Lan
    Zhongnan Daxue Xuebao (Ziran Kexue Ban)/Journal of Central South University (Science and Technology), 2014, 45 (09): : 2985 - 2992
  • [48] Effect of SRB on corrosion behavior of X80 pipeline steel
    Wan, Hong-Xia
    Li, Ting-Ting
    Song, Dong-Dong
    Chen, Chang-Feng
    Surface Technology, 2020, 49 (09): : 281 - 290
  • [49] Laboratory Investigation of Microbiologically Influenced Corrosion of X80 Pipeline Steel by Sulfate-Reducing Bacteria
    Cui, Liying
    Liu, Zhiyong
    Hu, Peng
    Shao, Jiamin
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2021, 30 (10) : 7584 - 7596
  • [50] Characterization of the effect of hydrogen sulfide on the corrosion of X80 pipeline steel in saline solution
    Zhao, Wei
    Zou, Yong
    Matsuda, Kenji
    Zou, Zengda
    CORROSION SCIENCE, 2016, 102 : 455 - 468
12345