Early-Age Cracking Resistance of Reinforced High- Strength Concrete

被引：0
|
作者：
Wen C. [1 ]
Shen D. [1 ]
Jiao Y. [2 ]
Liu C. [1 ]
Li M. [1 ]
机构：
[1] Hohai University, Nanjing
[2] Southeast University, Nanjing
来源：
ACI Structural Journal | 2024年 / 121卷 / 03期
关键词：
cracking resistance; early age; high-strength concrete (HSC); reinforcement; temperature-stress test machine (TSTM);
D O I：
10.14359/51740456
中图分类号：
学科分类号：
摘要：
High-strength concrete (HSC) with a low water-cement ratio (w/c) may experience large autogenous shrinkage (AS). When shrinkage of concrete is restrained by the subgrade, foundation, or other part of the structure, HSC is more prone to crack. However, studies devoted to the early-age cracking resistance of reinforced HSC under uniaxial restrained conditions and adiabatic conditions are still lacking. In the current research, the effect of reinforcement percentage and reinforcement configuration on the temperature history, shrinkage, stress, and creep behavior of reinforced HSC at early age was analyzed using the temperature-stress test machine. Test results showed that reinforcement could effectively restrain the development of concrete shrinkage and creep. The cracking resistance of HSC increased with increasing reinforcement percentage, evaluated by the integrated criterion. With the same reinforcement percentage, reinforced HSC with distributed reinforcement along with a proper thickness of concrete cover exhibited higher cracking resistance compared with that of central reinforcement. © 2024 American Concrete Institute. All rights reserved.
引用
收藏
页码：15 / 24
页数：9
相关论文
共 50 条
  • [21] CONTROL OF EARLY-AGE CRACKING IN WATERTIGHT CONCRETE STRUCTURES
    Matiaskova, Lydia
    Bilcik, Juraj
    Soltesz, Julius
    SLOVAK JOURNAL OF CIVIL ENGINEERING, 2018, 26 (03) : 16 - 21
  • [22] The Study on Cracking Strength of AIJs']Js to Release the Early-Age Stress of Mass Concrete
    Zhang, Xiaogang
    Wang, Chengqiang
    Wang, Shuping
    Xing, Feng
    Zhu, Ronghua
    ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2015, 2015
  • [23] THEORETICAL INVESTIGATION TO CRACKING PREDICTION OF EARLY-AGE CONCRETE
    Jin, Nanguo
    Bin, Yi
    Zhao, Yong
    Jin, Xianyu
    ADVANCES IN CONCRETE STRUCTURAL DURABILITY, PROCEEDINGS OF ICDCS2008, VOLS 1 AND 2, 2008, : 810 - 816
  • [24] Concrete early-age cracking control in engineering structures
    Li, Y. F.
    Qu, Z. J.
    ISISS '2007: PROCEEDINGS OF THE INNOVATION AND SUSTAINABILITY OF STRUCTURES, VOLS 1 AND 2, 2008, : 518 - 525
  • [25] A review on early-age cracking of concrete: Causes and control
    Qu, Zhiwei
    Zhang, Yingda
    Liu, Zihao
    Si, Ruizhe
    Wu, Jie
    Case Studies in Construction Materials, 2024, 21
  • [26] Limiting Early-Age Cracking in Concrete Bridge Decks
    ElSafty, Adel
    Abdel-Mohti, Ahmed
    Jackson, Mike
    Lasa, Ivan
    Paredes, Mario
    ADVANCES IN CIVIL ENGINEERING MATERIALS, 2013, 2 (01): : 379 - 399
  • [27] Modeling of Capillary Shrinkage and Cracking in Early-Age Concrete
    Leonovich, S. N.
    SCIENCE & TECHNIQUE, 2018, 17 (04): : 265 - 277
  • [28] Study on early-age cracking resistance of multi-scale polypropylene fiber reinforced concrete in restrained ring tests
    Liang, Ninghui
    Hu, Ganwen
    Zhou, Kan
    Liu, Xinrong
    Zhou, Xiaohan
    JOURNAL OF SUSTAINABLE CEMENT-BASED MATERIALS, 2024, 13 (07) : 1050 - 1062
  • [29] Early-Age Cracking Resistance of Multiscale Fiber-Reinforced Concrete with Steel Fiber, Sisal Fiber, and Nanofibrillated Cellulose
    Cao, Qi
    Zheng, Haibo
    Ju, He
    Lin, Zhibin
    Zhou, Changjun
    Jia, Jinqing
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2023, 35 (05)
  • [30] Effect of Nano-CaCO3 on Early-Age Properties and Cracking Potential of High-Strength Concrete
    Feng, Zhizhuo
    Shen, Dejian
    Xu, Shiqian
    Shao, Haoze
    Jiang, Guoqing
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2023, 35 (04)
12345