INFLUENCE OF COMBINED CHEMICAL-THERMAL TREATMENT MODES ON STRUCTURE FORMATION OF HIGH-SPEED STEEL

被引：0
|
作者：
Mukhammadjonovich B.J. [1 ]
Kizi P.M.M. [2 ]
Ugli E.M.S. [1 ]
机构：
[1] Mechanical Engineering Technologies Department, Belarusian-Uzbek Intersectoral Institute of Applied Technical Qualifications, Tashkent
[2] Kimyo International University, Tashkent
来源：
Int. J. Mech. Appl. Mech. | / 14卷 / 95-100期
关键词：
Hardening; High-speed steel; Microhardness; Nitro-carburization; Retained austenite; Tempering;
D O I：
10.17683/ijomam/issue14.12
中图分类号：
学科分类号：
摘要：
The paper presents the results of studies on the structure formation of R6M5 steel during heat treatment, which consists of hardening steel from generally accepted temperatures, and carrying out the process of low-temperature nitro-carburization combined with the tempering process. It has been established that the size of the austenite grain depends on the holding time when heating the steel for hardening, and the amount of retained austenite sharply decreases at a temperature of 550 °C and a holding time of 2.5 hours. © 2023, Cefin Publishing House. All rights reserved.
引用
收藏
页码：95 / 100
页数：5
相关论文
共 50 条
  • [31] Surface modification of steel 20 by the method of chemical-thermal treatment by annealing in a muffle furnace
    Shevchuk, E. P.
    Nurumkanov, D. K.
    Muratbekov, B. M.
    Ahmetzhanov, B.
    Plotnikov, V. A.
    BULLETIN OF THE UNIVERSITY OF KARAGANDA-PHYSICS, 2019, 3 (95): : 52 - 58
  • [32] INFLUENCE OF THE SIZE AND DISTRIBUTION OF CARBIDES ON THE TOUGHNESS OF A CONVENTIONAL HIGH-SPEED STEEL AND A HIGH-CARBON HIGH-SPEED STEEL
    LEVEQUE, R
    ELGHOZI, C
    JACURA, O
    MEMOIRES SCIENTIFIQUES DE LA REVUE DE METALLURGIE, 1980, 77 (01): : 69 - 82
  • [33] Diffusion coatings formation features, obtained by complex chemical-thermal treatment on the structural steels
    Sokolov, Aleksandr
    Bobylyov, Eduard
    Popov, Roman
    OBRABOTKA METALLOV-METAL WORKING AND MATERIAL SCIENCE, 2023, 25 (01): : 98 - 109
  • [34] Influence of heat treatment on content of the carbide phases in the microstructure of high-speed steel
    Jaworski J.
    Kluz R.
    Trzepieciński T.
    Jaworski, J. (jjktmiop@prz.edu.pl), 2017, De Gruyter Open Ltd (17) : 59 - 62
  • [35] Thermal treatment of cast carburized high-speed steel alloyed with Ti, Nb, and V
    Chaus, A.S.
    Murgash, M.
    Latyshev, I.V.
    Tot, R.
    Metallovedenie i Termicheskaya Obrabotka Metallov, 2001, (06): : 8 - 11
  • [36] High Isostatic Pressure Effect on the Structure of High-Speed Steel
    Taranova, M. A.
    Sanin, A. F.
    METALLOFIZIKA I NOVEISHIE TEKHNOLOGII, 2008, 30 : 743 - 751
  • [37] EFFECT OF THERMAL CYCLING TREATMENT ON THE STRUCTURE OF CAST HIGH-SPEED STEEL R6M5-Sh
    Khaidorov, A. D.
    Kondrat'ev, S. Yu.
    METAL SCIENCE AND HEAT TREATMENT, 2011, 53 (5-6) : 299 - 303
  • [38] Effect of thermal cycling treatment on the structure of cast high-speed steel R6M5-Sh
    A. D. Khaidorov
    S. Yu. Kondrat’ev
    Metal Science and Heat Treatment, 2011, 53 : 299 - 303
  • [39] METALLIC OXIDES WITH THE STRUCTURE OF HIGH-SPEED STEEL CARBIDE
    KARLSSON, N
    NATURE, 1951, 168 (4274) : 558 - 558
  • [40] Influence of Heat Treatment of High-Speed Steel on its Microstructure, Hardness and Fracture Toughness
    Cajner, Franjo
    Leskovsek, Vojteh
    Pustaic, Dragan
    MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE VII, 2014, 592-593 : 680 - 683
12345