The fatigue and fracture analysis of steam turbine rotor shafts containing defects

被引：1
|
作者：
Wang S. [1 ,2 ,3 ]
Wang W.Q. [1 ,2 ,3 ]
Song M.D. [2 ,4 ]
Zhang H. [2 ,4 ]
机构：
[1] School of Mechanical Engineering, Shandong University, Jinan
[2] Engineering and Technology Research Center for Special Equipment Safety of Shandong Province, Jinan
[3] Research Center of Safety Guarantee and Assessment to Special Equipment, Shandong University, Jinan
[4] Shandong Special Equipment Inspection and Research Academy Corporation, Jinan
来源：
Key Engineering Materials | 2019年 / 795卷
关键词：
Defect; Steam turbine rotor shafts; Stress analysis; The fatigue crack propagation life;
D O I：
10.4028/www.scientific.net/KEM.795.254
中图分类号：
学科分类号：
摘要：
In this study, the assessment and calculation methods for the crack propagation life of steam turbine rotor shafts containing defects are presented. The analytic methods for estimating the average stress and the alternating stress amplitude of the steam turbine rotor shafts are introduced. The defects on/in the rotor shafts were regularized by the method of fracture mechanics, and the high cycle fatigue crack propagation life and low cycle fatigue crack propagation life of the rotor shafts are estimated from Paris formula. Taking the 60MW turbine rotor shafts containing an initial surface defect and an initial internal defect as the examples respectively, the crack propagation life of them were calculated. The results indicated that the assessment method for the crack propagation life can preliminarily be both used to estimate the safety-operating life and to analyze the fracture reason of a steam turbine rotor shaft containing defects. This paper can provide reference for periodic maintenance and safety evaluation of turbine rotor shafts. © 2019 Trans Tech Publications Ltd, Switzerland.
引用
收藏
页码：254 / 261
页数：7
相关论文
共 50 条
  • [31] Assessment of Low Cycle Fatigue Life of Steam Turbine Rotor Based on a Thermodynamic Approach
    Sun, Yong-Jian
    Hu, Li-Sheng
    JOURNAL OF ENGINEERING FOR GAS TURBINES AND POWER-TRANSACTIONS OF THE ASME, 2012, 134 (06):
  • [32] Simulation of residual stress in welded steam turbine rotor and its effects on fatigue life
    Feng, Lei
    Liu, Xia
    Xuan, Fuzhen
    Zhongguo Dianji Gongcheng Xuebao/Proceedings of the Chinese Society of Electrical Engineering, 2014, 34 (17): : 2851 - 2860
  • [33] Considerations to the an-isothermal creep-fatigue assessment of steam turbine rotor steels
    Reigl, Martin
    Dave, Harish N.
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE 2007, VOL 9, 2008, : 267 - 274
  • [34] Peculiarities of fatigue fracture of high-alloyed heat-resistant steel after its operation in steam turbine rotor blades
    Krechkovska, H.
    Hredil, M.
    Student, O.
    Svirska, L.
    Krechkovska, S.
    Tsybailo, I.
    Solovei, P.
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 167
  • [35] PREVENTION OF STEAM TURBINE ROTOR DISTORTION
    TRUBILOV, MA
    PROKHORO.SA
    ZHURAVLE.RV
    KULICHIK.VV
    THERMAL ENGINEERING, 1969, 16 (05) : 56 - &
  • [36] Analysis of Torsional Stress and Fatigue of Turbine-Generator Shafts during Islanding
    Babi, Bombay
    Bokoro, Pitshou
    2020 IEEE PES & IAS POWERAFRICA CONFERENCE, 2020,
  • [37] Fretting fatigue induced surface cracks under shrink fitted main bearings in wind turbine rotor shafts
    Rauert, Thes
    Herrmann, Jenni
    Dalhoff, Peter
    Sander, Manuela
    21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21), 2016, 2 : 3601 - 3609
  • [38] Analysis on corrosion fatigue cracking mechanism of 17-4PH blade of low pressure rotor of steam turbine
    Wei, Yuwei
    Li, Yongjun
    Lai, Jiafeng
    Zhao, Qinxin
    Yang, Lili
    Lin, Qingyu
    Wang, Xiaolin
    Pan, Zhi
    Lin, Zhu
    ENGINEERING FAILURE ANALYSIS, 2020, 118
  • [39] ON THE SENSITIVITY MULTIPLICATION FACTOR OF THE ULTRASONIC TESTING OF TURBINE ROTOR SHAFTS
    KIMURA, K
    TRANSACTIONS OF NATIONAL RESEARCH INSTITUTE FOR METALS, 1980, 22 (01): : 19 - 22
  • [40] Multimode Tip-Timing Analysis of Steam Turbine Rotor Blades
    Manerowski, Jerzy
    Rzadkowski, Romuald
    Kowalski, Miroslaw
    Szczepanik, Ryszard
    IEEE SENSORS JOURNAL, 2023, 23 (11) : 11721 - 11728
12345