Research on preparation of high-entropy composite coating reinforced by endogenous alumina particles and its anti-friction performance

被引:0
|
作者
Tang Q.-Y. [1 ]
Ji X.-L. [1 ]
Duan J. [1 ]
Wang H. [1 ]
Zhang Y.-T. [1 ]
机构
[1] College of Mechanical and Electrical Engineering, Hohai University, Changzhou
来源
Surface Technology | 2021年 / 50卷 / 11期
基金
中国国家自然科学基金;
关键词
Al[!sub]2[!/sub]O[!sub]3[!/sub; Friction; High-entropy composite coating; Wear resistance;
D O I
10.16490/j.cnki.issn.1001-3660.2021.11.022
中图分类号
学科分类号
摘要
This paper is to study the effect of Al content on the microstructure and tribology performance of high-entropy composite coating reinforced by endogenous alumina particles. In the process of laser cladding, metal oxides were reduced and deposited on the surface of Q235 steel by thermite reaction to prepare AlxCoCrFeNi (x=0, 0.3, 1, 1.5, 2) high-entropy composite coating reinforced by endogenous Al2O3 ceramic particles. XRD, SEM, EDS, XPS, RAMAN, friction test and other experimental methods were used to study the microstructure and tribology performance of the high-entropy composite coatings. The results show that there are dispersed nano-sized Al2O3 ceramic particles in the coating. With the increase of Al content, the microstructure of the high-entropy composite coating gradually changes from FCC and BCC coexistence to BCC single phase. At the same time, the friction coefficient and wear rate of the high-entropy composite coating under 10 N load decreased with the increase of Al content. Al2CoCrFeNi has the lowest friction coefficient (0.15) and the lowest wear rate (1.01×10–6 mm3/(N·m)), which are 1/4 and 1/38 of the base Q235 steel respectively. When x in AlxCoCrFeNi coating increases to 2, the peeling phenomenon of the wear scar surface disappears. The main wear form of the coating changes from oxidative wear and fatigue wear to slight abrasive wear. The average friction coefficient of Al2CoCrFeNi coating increased to 0.325 under a load of 20 N. Increasing the Al element in the composite coating can stabilize the BCC phase and refine the structure. At the same time, excessive Al element can inhibit Fe element oxidation and increase the content of Fe3O4 on the surface of the wear scar, thereby significantly reducing the friction coefficient of the composite coating and improving its friction reduction and wear resistance. © 2021, Chongqing Wujiu Periodicals Press. All rights reserved.
引用
收藏
页码:218 / 225
页数:7
相关论文
共 27 条
  • [21] ZHAO Liang, HPHT synthesis and characterization of NaAlSi2O6 jadeite doped with different oxides, (2020)
  • [22] WANG Jing, The synthesis of iron oxide composites and their application in the remediation of polycyclic aromatic hydrocarbon contaminated soil, (2019)
  • [23] GAO Peng, Raman spectroscopy of residual stress of alumina coating and its application, (2019)
  • [24] GAO M S., Preparation of hollow transition metal(Fe, Co, Ni)hydroxides and oxides for SERS applications, (2019)
  • [25] YUAN Hui, XU Guang-tong, QIHERIMA, Et al., Laser Raman spectra study on Co-Mo/Al2O3 hydrodesulphurization catalysts, Spectroscopy and spectral analysis, 34, 2, pp. 435-438, (2014)
  • [26] HAN Yin-long, SUN Wen-bo, TIAN Xiang-yu, Et al., Preparation and characterization of in situ grapheme coated metal particle, New chemical materials, 47, 4, pp. 84-88, (2019)
  • [27] HAO Ying-ying, Preparation and application of nickel molybdate and its composites, (2019)