Effect of Cr Addition on Corrosion Resistance of Laser-Cladding Ni-Cr-Mo Coatings in Chloride Solution with Thiosulfate

被引：0
|
作者：
Liu, Quanbing [1 ]
Liu, Zongde [1 ]
Wang, Yongtian [1 ]
Kong, Yao [1 ]
Ma, Herong [1 ]
Li, Yue [1 ]
机构：
[1] Key Laboratory of Power Station Energy Transfer Conversion and System of Ministry of Education, North China Electric Power University, Beijing,102206, China
来源：
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering | 2023年 / 52卷 / 04期
关键词：
Chlorine compounds - Chromium alloys - Chromium compounds - Corrosion resistance - Corrosion resistant coatings - Iron alloys - Laser cladding - Molybdenum alloys - Scanning electron microscopy - Solid solutions - Ternary alloys;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The effect of Cr addition on the corrosion resistance of the laser-cladding Ni-Cr-Mo coatings was evaluated in chloride solution with thiosulfate by microstructure observation and electrochemical measurements. Results show that very similar microstructures and phase compositions are tested by scanning electron microscope and X-ray diffraction. Both eutectic and dendrite structures are observed, and the coatings are mainly composed of the γ-Ni solid solution of Cr, Mo, W, Fe, and Cr0.19Fe0.7Ni0.11 solid solution. The electrochemical results confirm that the laser-cladding coating with the special Cr addition behaves better corrosion resistance. The coating C28 performs higher values in open circuit potential and lower passive current density, especially the larger modulus of the impedance and charger transfer resistance. With increasing Cr content, the passive film is much thicker and the defects of the films are less in chloride solution with thiosulfate. The Mott-Schottky reveals that the passive film formed on the top surface of the laser-cladding coatings in solution behaves as n-type and p-type semiconductors. Copyright © 2023, Northwest Institute for Nonferrous Metal Research. Published by Science Press. All rights reserved.
引用
收藏
页码：1210 / 1218
相关论文
共 50 条
  • [31] DISCUSSION OF RELATIONSHIP OF HEAT TREATMENT + MICROSTRUCTURE TO CORROSION RESISTANCE IN WROUGHT NI-CR-MO ALLOYS
    HELLER, HF
    STREICHER, MA
    CORROSION, 1964, 20 (12) : 3 - &
  • [32] The effect of Cr content on the corrosion resistance of WC-Ni-Cr-Mo composites
    Santos, R. F.
    Rocha, A. M. Ferro
    Bastos, A. C.
    Cardoso, J. P.
    Rodrigues, F.
    Fernandes, C. M.
    Sacramento, J.
    Ferreira, M. G. S.
    Senos, A. M. R.
    Fonseca, C.
    Vieira, M. F.
    Malheiros, Luis F.
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2021, 95
  • [33] Effect of composition on the solidification behavior of several Ni-Cr-Mo and Fe-Ni-Cr-Mo alloys
    Perricone, MJ
    Dupont, JN
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2006, 37A (04): : 1267 - 1280
  • [34] Effect of composition on the solidification behavior of several Ni-Cr-Mo and Fe-Ni-Cr-Mo alloys
    M. J. Perricone
    J. N. Dupont
    Metallurgical and Materials Transactions A, 2006, 37 : 1267 - 1280
  • [35] Tribological behavior of laser-cladding Ni60 and Co-Cr-W coatings at elevated temperature
    Cai, Zhen-bing
    Zhu, Min-hao
    Lin, Xiu-zhou
    Mo, Ji-liang
    Zhou, Zhong-rong
    PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 : 878 - 881
  • [36] Cause of Ni-Cr-Mo weld metal corrosion questioned - Reply
    Hodge, FG
    MATERIALS PERFORMANCE, 1997, 36 (12) : 7 - 8
  • [37] Effect of saccharin addition on formation, wear and corrosion resistance of electrodeposited Ni-Cr coatings
    Demir, Mehmet
    Kanca, Erdogan
    Karahan, Ismail Hakki
    MATERIALS SCIENCE-POLAND, 2023, 41 (03) : 111 - 125
  • [38] Corrosion Characteristics of Typical Ni-Cr Alloys and Ni-Cr-Mo Alloys in Supercritical Water: A Review
    Guo, Shuwei
    Xu, Donghai
    Liang, Yu
    Li, Yanhui
    Yang, Jianqiao
    Chen, Gang
    Macdonald, Digby D.
    INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2020, 59 (42) : 18727 - 18739
  • [39] In Operando Analysis of Passive Film Growth on Ni-Cr and Ni-Cr-Mo Alloys in Chloride Solutions
    Cwalina, Katie Lutton
    Ha, Hung M.
    Ott, Noemie
    Reinke, Petra
    Birbilis, Nick
    Scully, John R.
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2019, 166 (11) : C3241 - C3253
  • [40] Effect of solution treatment on the hot workability of electroslag remelted Ni-Cr-Mo alloy
    Kim, TK
    Jang, J
    Hong, JH
    METALS AND MATERIALS INTERNATIONAL, 2002, 8 (01): : 45 - 51
12345