Research advances of stainless-clad bimetallic steel structures

被引：1
|
作者：
Ban H.-Y. [1 ]
Mei Y.-X. [1 ]
Shi Y.-J. [1 ]
机构：
[1] Department of Civil Engineering, Tsinghua University, Beijing
来源：
Ban, Hui-Yong (banhy@tsinghua.edu.cn) | 1600年 / Tsinghua University卷 / 38期
关键词：
Engineering application; Literature review; Manufacture; Mechanical properties; Stainless-clad bimetallic steel;
D O I：
10.6052/j.issn.1000-4750.2020.04.ST01
中图分类号：
学科分类号：
摘要：
The stainless-clad (SC) bimetallic steel combines the excellent corrosion resistance of stainless steel with the high strength and low cost of conventional mild (CM) steel. It possesses better comprehensive mechanical properties and may lead to a shorter construction period, longer design service life, lower full-life cycle cost and higher social benefits, and therefore great potential is expected for the utilization in engineering structures with high requirements on corrosion resistance. At present, the SC bimetallic steel has been successfully used in high-rise building curtain walls and railway steel bridge decks. In order to further promote its application and development in the field of structural engineering, more research and discussions are urgently needed from the perspective of fundamental mechanical properties and engineering techniques. This article provides a comprehensive review of studies on manufacturing, engineering practice as well as mechanical properties of the SC bimetallic steel at material and component levels, including the tensile properties, bending properties, high temperature properties, fracture and fatigue properties, cyclic loading properties, high-strain rate properties, corrosion resistance, bonding interface performance, structural stability, residual stress, welded joint, defect repair as well as finite element modeling. It is expected to provide a reference for further research, design and application of the SC bimetallic steel in the field of structural engineering. Copyright ©2021 Engineering Mechanics. All rights reserved.
引用
收藏
页码：1 / 23
页数：22
相关论文
共 179 条
  • [81] Nambu S, Michiuchi M, Inoue J, Et al., Effect of interfacial bonding strength on tensile ductility of multilayered steel composites, Composites Science and Technology, 69, 11, pp. 1936-1941, (2009)
  • [82] Huang Q X, Yang X R, Ma L F, Et al., Interface-correlated characteristics of stainless steel/carbon steel plate fabricated by AAWIV and hot rolling, Journal of Iron and Steel Research(International), 21, 10, pp. 931-937, (2014)
  • [83] Li H, Zhang L Y, Zhang B Y, Et al., Interfacial fracture behavior of a stainless/carbon steel bimetal plate in a uniaxial tension test, Results in Physics, 14, (2019)
  • [84] Li H, Zhang L Y, Zhang B Y., Interfacial fracture morphologies of stainless steel clad plates after uniaxial tension, 5th International Conference on Energy Materials and Environment Engineering (ICEMEE), (2019)
  • [85] Liu B X, An Q, Yin F X, Et al., Interface formation and bonding mechanisms of hot-rolled stainless steel clad plate, Journal of Materials Science, 54, 17, pp. 11357-11377, (2019)
  • [86] Dhib Z, Guermazi N, Gasperini M, Et al., Cladding of low-carbon steel to austenitic stainless steel by hot-roll bonding: Microstructure and mechanical properties before and after welding, Materials Science & Engineering A, 656, pp. 130-141, (2016)
  • [87] Zheng Yuanmou, Press working of explosive welded composite material metals, Research on Iron and Steel, 3, pp. 32-37, (1999)
  • [88] Liu B X, Yin F X, Dai X L, Et al., The tensile behaviors and fracture characteristics of stainless steel clad plates with different interfacial status, Materials Science & Engineering A, 679, pp. 172-182, (2017)
  • [89] He J Y, Ma Y, Yan D S, Et al., Improving ductility by increasing fraction of interfacial zone in low C steel/304 SS laminates, Materials Science & Engineering A, 726, pp. 172-182, (2018)
  • [90] Chen C X, Liu M Y, Liu B X., Microstructures and tensile behaviors of stainless steel clad plate [C], Chinese Materials Conference 2017, (2017)
45678910111213