In-plane deformation behavior of unidirectional carbon fiber/epoxy prepreg layups

被引：0
|
作者：
Chen P. [1 ,2 ]
Zhao Y. [1 ]
Chen F. [2 ]
Zhang B. [1 ]
机构：
[1] School of Materials Science and Engineering, Beihang University, Beijing
[2] Composite Center, Shanghai Aircraft Manufacturing Corporation Ltd., Shanghai
来源：
Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica | 2020年 / 37卷 / 05期
关键词：
Bias extension method; Deformation mechanism; Hot diaphragm forming; Pin-joined net(PJN) theory; Unidirectional thermoset prepreg;
D O I：
10.13801/j.cnki.fhclxb.20190730.006
中图分类号：
学科分类号：
摘要：
In order to fully understand the deformation behavior of prepreg in the process of hot diaphragm forming, the in-plane deformation mechanism of unidirectional carbon fiber/epoxy thermoset prepreg at high temperature was studied using the bias extension method. The effects of testing temperature, tensile rate, preheating time and stacking sequence on the in-plane deformation were investigated. Using digital image correlation technology, the specimen deformation and fiber rotation were captured during testing process. The results show that increasing temperature or decreasing tensile rate can promote the deformation of unidirectional carbon fiber/epoxy thermoset prepreg. Stacking sequence has a great influence on the deformation behavior of the unidirectional carbon fiber/epoxy thermoset prepreg stacks. The fiber rotation of [45/-45/90]S layup is easier than that of [45/90/-45]S layup, and the former has lower deformation resistance. The Pin-joined net (PJN) theory was used to predict the fiber rotation angle during the deformation process of the unidirectional carbon fiber/epoxy thermoset prepreg stacks, and the prediction value was compared with the experiment value. The results show that the prediction values deviate greatly from the experiment values, indicating that the PJN theory is not suitable for the prediction of the fiber rotation angle during the deformation of unidirectional carbon fiber/epoxy thermoset prepreg. Being preheated at 80℃ can increase the deformation resistance of the prepreg. © 2020, Editorial Office of Acta Materiae Compositae Sinica. All right reserved.
引用
收藏
页码：1049 / 1055
页数：6
相关论文
共 19 条
  • [11] LEBRUN G, BUREAU M N, DENAULT J., Evaluation of bias-extension and picture-frame test methods for the measurement of intraply shear properties of PP/glass commingled fabrics, Composite Structures, 61, 4, pp. 341-352, (2003)
  • [12] POTTER K., Beyond the pin-jointed net: Maximising the deformability of aligned continuous fibre reinforcements, Composites Part A: Applied Science and Manufacturing, 33, 5, pp. 677-686, (2002)
  • [13] HARRISON P, CLIFFORD M J, LONG A C., Shear characterization of viscous woven textile composites: A comparison between picture frame and bias extension experiments, Composites Science and Technology, 64, 10-11, pp. 1453-1465, (2004)
  • [14] LARBERY Y, AKERMO M., In-plane deformation of multi-layered unidirectional thermoset prepreg: Modelling and experimental verification, Composites Part A: Applied Science and Manufacturing, 56, pp. 203-212, (2014)
  • [15] POTTER K., In-plane and out-of-plane deformation properties of unidirectional preimpregnated reinforcement, Composites Part A: Applied Science and Manufacturing, 33, 11, pp. 1469-1477, (2002)
  • [16] LARBERY Y R, AKERMO M, NORRBY M., On the in-plane deformability of cross-plied unidirectional prepreg, Journal of Composite Materials, 46, 8, pp. 929-939, (2009)
  • [17] CHEN Jie, GU Yizhuo, LI Min, Et al., Measurement and evolution of frictional slipping behavior of carbon fiber/epoxy prepreg, Acta Materiae Compositae Sinica, 31, 1, pp. 101-106, (2014)
  • [18] BIAN Xuxia, GU Yizhuo, SUN Jing, Et al., Effect of temperature and molding rate in hot diaphragm forming process n the forming quality of C-shaped composite, Fiber Reinforced Plastics/Composites, 5, pp. 45-50, (2013)
  • [19] KIM D, CENTEA T, NUTT S R., Out-time effects on cure kinetics and viscosity for an out-of-autoclave (OOA) prepreg: Modelling and monitoring, Composites Science and Technology, 100, pp. 63-69, (2014)
12