Influence of Ultraviolet Light and Alternating Wet-Dry Environments on the Corrosion Behavior of Weathering Steels

被引：0
|
作者：
Yang, Ying [1 ,2 ]
Wang, Yubo [1 ,2 ]
Du, Xinyu [3 ]
Lin, Tianzi [1 ,2 ]
Wang, Han [3 ]
Meng, Fandi [3 ]
Wang, Fuhui [3 ]
机构：
[1] State Key Lab Met Mat Marine Equipment & Applicat, Anshan 114009, Peoples R China
[2] Iron & Steel Res Inst, Anshan Iron & Steel Grp, Anshan 114009, Peoples R China
[3] Northeastern Univ, Shenyang Natl Lab Mat Sci, Wenhua Rd 3-11, Shenyang 110819, Peoples R China
来源：
MATERIALS | 2024年 / 17卷 / 15期
基金：
中国国家自然科学基金;
关键词：
weathering steel; ultraviolet; alternating wet and dry conditions; ATMOSPHERIC CORROSION; CARBON-STEEL;
D O I：
10.3390/ma17153870
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The corrosion behaviors of two bridge steels (Q345q and Q500q) under simulated ultraviolet irradiation and a wet-dry alternating (UVWD) environment were studied. Weight loss measurement, stereomicroscope observation, SEM, XRD, and electrochemical impedance spectroscopy (EIS) were performed to investigate the influence of the coupled environment. The results revealed that the corrosion rates of Q345q and Q500q were significantly accelerated by the synergistic effect of UV light exposure and alternating wet-dry conditions. Numerous voids and cracks could be observed throughout the thickened rust layers, enabling the corrosive substances to easily penetrate through the rust layer. Q500q exhibited better corrosion resistance than Q345q due to the addition of Mo, Cr, and Ni as corrosion-resistant elements, which tended to transform the rust layer into alpha-FeOOH rather than gamma-FeOOH during later stages of corrosion.
引用
收藏
页数：15
相关论文
共 50 条
  • [21] Degradation behavior and mechanism of slate under alternating conditions of freeze-thaw and wet-dry
    Wu G.
    Chen W.
    Cui K.
    Wang P.
    Zhongnan Daxue Xuebao (Ziran Kexue Ban)/Journal of Central South University (Science and Technology), 2019, 50 (06): : 1392 - 1402
  • [22] Hydrogen permeation behavior and corrosion monitoring atmospheric of steel in cyclic wet-dry environment
    Zheng, C.
    Huang, Y.
    Huo, C.
    Yu, Q.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2007, 58 (09): : 696 - 700
  • [23] Corrosion Behavior of E690 High-Strength Steel in Alternating Wet-Dry Marine Environment with Different pH Values
    W. Wu
    W. K. Hao
    Z. Y. Liu
    X. G. Li
    C. W. Du
    W. J. Liao
    Journal of Materials Engineering and Performance, 2015, 24 : 4636 - 4646
  • [24] Corrosion Behavior of Q235A Steel under Wet-dry Cyclic Condition
    Liu Jian Guo
    Li Yan Tao
    Hou Bao Rong
    ADVANCED MATERIALS AND PROCESSES II, PTS 1-3, 2012, 557-559 : 139 - +
  • [25] Corrosion Behavior of E690 High-Strength Steel in Alternating Wet-Dry Marine Environment with Different pH Values
    Wu, W.
    Hao, W. K.
    Liu, Z. Y.
    Li, X. G.
    Du, C. W.
    Liao, W. J.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2015, 24 (12) : 4636 - 4646
  • [26] Mossbauer and XRD analysis of corrosion products on weathering steel treated by wet-dry cycles using various solutions
    Oyabu, Matashige
    Nomura, Kiyoshi
    Koike, Yuya
    Okazawa, Atsushi
    HYPERFINE INTERACTIONS, 2016, 237 : 1 - 7
  • [27] Environmental embrittlement of automobile spring steels caused by wet-dry cyclic corrosion in sodium chloride solution
    Komazaki, S
    Kobayashi, K
    Misawa, T
    Fukuzumi, T
    CORROSION SCIENCE, 2005, 47 (10) : 2450 - 2460
  • [28] The Release and Migration of Cr in the Soil under Alternating Wet-Dry Conditions
    Chen, Zhe
    Chen, Ying
    Liang, Jing
    Sun, Zhiyu
    Zhao, Haoren
    Huang, Yi
    TOXICS, 2024, 12 (02)
  • [29] Unfolding the dynamics of ecosystems undergoing alternating wet-dry transitional states
    Arias-Real, Rebeca
    Delgado-Baquerizo, Manuel
    Sabater, Sergi
    Gutierrez-Canovas, Cayetano
    Valencia, Enrique
    Aragon, Gregorio
    Canton, Yolanda
    Datry, Thibault
    Giordani, Paolo
    Medina, Nagore G.
    de los Rios, Asuncion
    Romani, Anna M.
    Weber, Bettina
    Hurtado, Pilar
    ECOLOGY LETTERS, 2024, 27 (08)
  • [30] INFLUENCE OF WEATHERING ON THE CORROSION BEHAVIOR OF UNALLOYED AND LOW-ALLOY STEELS
    SCHWITTER, H
    BOHNI, H
    WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1980, 31 (09): : 703 - 711
12345