Verification of the Properties of Zinc Hot-Dip Galvanized Steel Samples

被引：0
|
作者：
Cerny, Daniel [1 ]
Kuchar, Jiri [1 ]
Kania, Henryk [2 ]
Saternus, Mariola [2 ]
机构：
[1] Czech Tech Univ, Prague, Czech Republic
[2] Silesian Tech Univ, Gliwice, Poland
来源：
ADVANCES IN MANUFACTURING IV, VOL 1, MANUFACTURING 2024 | 2024年
关键词：
Hot-dip Galvanizing; Zinc; Coating Thickness; BATH TEMPERATURE; COATINGS;
D O I：
10.1007/978-3-031-56463-5_15
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Zinc hot-dip galvanizing is one of the oldest methods of protection against corrosion. The goal of this study was to evaluate the influence of zinc bath temperature and immersion time on the coating quality. Three values of bath temperatures and two immersion times were selected. The surface roughness was measured with a surface roughness tester. The corrosion resistance of the samples was evaluated by salt spray corrosion test. The coating thickness was measured with a thickness gauge. The microstructure of the coatings was analyzed, and coating thickness values verified by image analysis methods.
引用
收藏
页码：195 / 205
页数：11
相关论文
共 50 条
  • [1] THE PROBLEM WITH THE ZINC COATING DIVERSIFICATION OF THE HOT-DIP GALVANIZED STEEL
    Wegrzynkiewicz, Sylwia
    [J]. METAL 2015: 24TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2015, : 916 - 922
  • [2] ADHERENCE OF ZINC COATINGS ON HOT-DIP GALVANIZED STEEL WIRES
    FUNKE, P
    PAVLIDIS, C
    [J]. STAHL UND EISEN, 1972, 92 (18): : 867 - &
  • [3] COATINGS FOR HOT-DIP GALVANIZED STEEL
    VANOETER.KA
    [J]. FETTE SEIFEN ANSTRICHMITTEL VERBUNDEN MIT DER ZEITSCHRIFT DIE ERNAHRUNGSINDUSTRIE, 1971, 73 (12): : 717 - &
  • [4] Failure of Hot-Dip Galvanized Steel Parts
    Panzenboeck, M.
    Mendez-Martin, Francisca
    Rashkova, Boryana
    Schuetz, Patric
    Kaiser, Robert
    [J]. PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY, 2016, 53 (10): : 641 - 651
  • [5] CHINESE HOT-DIP GALVANIZED STEEL CONSUMPTION
    [J]. China Nonferrous Metals Monthly, 1997, (03) : 4 - 6
  • [6] Cracks in Hot-Dip Galvanized Steel Components
    Freitag, C.
    Panzenboeck, M.
    [J]. PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY, 2017, 54 (06): : 408 - 419
  • [7] HOT-DIP GALVANIZED STEEL - PRODUCT OF THE FUTURE
    CHILAUD, M
    MATTIEU, S
    PICHANT, P
    QUINCHON, G
    JUNGMANN, B
    [J]. CIM BULLETIN, 1986, 79 (890): : 86 - 86
  • [8] Embrittlement of Hot-Dip Galvanized Steel: A Review
    Shreyas, P.
    Panda, Bijayani
    Vishwanatha, A. D.
    [J]. 3RD INTERNATIONAL CONFERENCE ON ADVANCEMENTS IN AEROMECHANICAL MATERIALS FOR MANUFACTURING: ICAAMM-2020, 2021, 2317
  • [9] TITANIUM ZINC AND HOT-DIP GALVANIZED STEEL - PREFERRED MATERIALS IN EUROPEAN ARCHITECTURE
    PLAWER, HL
    [J]. METALL, 1993, 47 (09): : 842 - &
  • [10] INFLUENCE OF MARTENSITE ON MECHANICAL PROPERTIES OF HOT-DIP GALVANIZED TRIP STEEL
    Ding Wei
    Tang Di
    Hang Haitao
    Huang Wei
    [J]. ACTA METALLURGICA SINICA, 2010, 46 (05) : 595 - 599
12345