Cracks in Hot-Dip Galvanized Steel Components

被引：2

作者：

Freitag, C. ^{[1
]}

Panzenboeck, M. ^{[1
]}

机构：

[1] Univ Leoben, Dept Met Kunde & Werkstoffprufung, Roseggerstr 12, A-8700 Leoben, Austria

来源：

PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY | 2017年 / 54卷 / 06期

关键词：

Galvanizing;

D O I：

10.3139/147.110452

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Again and again, components fail due to sudden crack initiation. In the present case, a hot-dip galvanized structural hollow section failed. It was manufactured from unal-loyed structural steel of the type S355J0. Hydrogen plays a decisive role in this failure which results from a time-delayed damage of the material.

引用

页码：408 / 419

页数：12

共 50 条

[1] On the bonding of hot-dip galvanized components
Abeln, Bjoern
Richter, Carl
Feldmann, Markus
[J]. STAHLBAU, 2017, 86 (11) : 1029 - 1035
[2] COATINGS FOR HOT-DIP GALVANIZED STEEL
VANOETER.KA
[J]. FETTE SEIFEN ANSTRICHMITTEL VERBUNDEN MIT DER ZEITSCHRIFT DIE ERNAHRUNGSINDUSTRIE, 1971, 73 (12): : 717 - &
[3] Adhesion of batch hot-dip galvanized components
Abeln, Bjoern
Pinger, Thomas
Richter, Carl
Feldmann, Markus
[J]. INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2023, 125 (11-12): : 5197 - 5209
[4] Adhesion of batch hot-dip galvanized components
Björn Abeln
Thomas Pinger
Carl Richter
Markus Feldmann
[J]. The International Journal of Advanced Manufacturing Technology, 2023, 125 (11-12) : 5197 - 5209
[5] Failure of Hot-Dip Galvanized Steel Parts
Panzenboeck, M.
Mendez-Martin, Francisca
Rashkova, Boryana
Schuetz, Patric
Kaiser, Robert
[J]. PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY, 2016, 53 (10): : 641 - 651
[6] CHINESE HOT-DIP GALVANIZED STEEL CONSUMPTION
[J]. China Nonferrous Metals Monthly, 1997, (03) : 4 - 6
[7] Embrittlement of Hot-Dip Galvanized Steel: A Review
Shreyas, P.
Panda, Bijayani
Vishwanatha, A. D.
[J]. 3RD INTERNATIONAL CONFERENCE ON ADVANCEMENTS IN AEROMECHANICAL MATERIALS FOR MANUFACTURING: ICAAMM-2020, 2021, 2317
[8] HOT-DIP GALVANIZED STEEL - PRODUCT OF THE FUTURE
CHILAUD, M
MATTIEU, S
PICHANT, P
QUINCHON, G
JUNGMANN, B
[J]. CIM BULLETIN, 1986, 79 (890): : 86 - 86
[9] Prediction of fatigue resistance of a hot-dip galvanized steel
Vogt, JB
Boussac, O
Foct, J
[J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2001, 24 (01) : 33 - 39
[10] ATMOSPHERIC CORROSION BEHAVIOR OF HOT-DIP GALVANIZED AND CONTINUOUS GALVANIZED STEEL
Sigircik, Gokmen
Yildirim, Omer
Tuken, Tunc
[J]. ACTA METALLURGICA SLOVACA, 2022, 28 (03): : 117 - 126

← 1 2 3 4 5 →