Development of an active biogenic silver nanoparticles composite film based on berry wax and chitosan for rabbit meat preservation

This study aimed to develop an eco-friendly active biogenic nanocomposite film through the complexation of silver nanoparticles (AgNPs), berry wax (BYW), and chitosan (CT) for maintiaing rabbit functional meat freshness. AgNPs were synthesized using Chinese medicinal paeoniaceae petal extract, and they were loaded at various concentrations (0.5 %, 0.75 %, 1.0 %, 1.25 %, and 1.5 % based on CT w/w) into the CT/BYW complex. The AgNPs exhibited an average size of 55 nm and a zeta potential of -26.3 mV with a spherical shape. The particle size and zeta potential of the film dispersions were 370.5-529.5 nm and 40.17-49.345 mV, respectively. FTIR, SEM, and XRD results showed compatibility among AgNPs and CT/BYW structure. The film water vapor permeability and light transparency decreased from 6.5 to 3.5 and 10 to 0.78 %, respectively, while opacity increased from 1.76 to 9.96 % with increasing concentrations of AgNPs. Among them, the film composite CT/ BYW/AgNPs1.5% had better antioxidant and antibacterial properties, which was then applied for rabbit meat preservation at 4 degrees C for 16 days of storage. CT/BYW/AgNPs1.25%-packed sample had lower values of TVB-N, TBARS, TVC, and pH with greater retention of color properties compared to the control sample, which describes its ability to maintain meat freshness.