Deciphering the catalytic activity of nickel anchored on Fe3O4@SiO2@3-CPMS@L as a magnetically recoverable nanocatalyst for the efficacious reduction of 4-nitrophenol, nitrobenzene, and methyl orange

In this paper, a versatile heterogeneous nanocatalyst was fabricated employing a self-assembly technique. To commence, Fe3O4 MNPs were coated with a thin layer of SiO2 using the stobbers method. Subsequently, the surface was further functionalized with 3-CPMS, followed by a reaction with a Schiff base. Finally, nickel NPs were deposited on the surface through in situ deposition, forming the Fe3O4@SiO2@3-CPMS@L-Ni magnetic nanocatalyst. The architecture of this magnetic nanocatalyst was meticulously characterized through an array of sophisticated techniques: XRD, FT-IR, SEM, TEM, BET and VSM. The XRD diffraction pattern confirmed the presence of Fe3O4 MNPs, SiO2, and Ni peaks, providing evidence for successful synthesis. Moreover, the successful functionalization with a Schiff base was demonstrated by the presence of an azomethane peak in the FTIR spectra of the synthesized nanocatalyst. The fabricated nanocatalyst was adeptly utilized for the reduction of 4NP, NB, and MO demonstrating a remarkably elevated rate of catalytic efficacy. Moreover, this catalyst was effortlessly retrievable through the application of an external magnet, and it maintained its catalytic prowess across at least six consecutive cycles. The utilization of water as an environmentally friendly solvent, coupled with the utilization of abundant and cost-effective nickel catalyst instead of the costly Pd or Pt catalysts, along with the successful recovery and scalability of the catalyst, render this method highly advantageous from both environmental and economic perspectives for the reduction of 4-NP, NB, and MO.