The role of hydrogen on lead-induced localized corrosion of Alloy 690TT

被引：0
|
作者：
Li, Weipeng [1 ,2 ]
Mi, Zhishan [1 ]
He, Yang [1 ]
Han, Yaolei [2 ]
Shi, Fangjie [2 ]
Peng, Qunjia [2 ]
Qiao, Lijie [1 ]
机构：
[1] Univ Sci & Technol Beijing, Beijing Adv Innovat Ctr Mat Genome Engn, Beijing 100083, Peoples R China
[2] Suzhou Nucl Power Res Inst, Suzhou 215004, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 240卷
基金：
中国国家自然科学基金;
关键词：
Lead; Hydrogen; Nickel-based alloy; Passive film; Localized corrosion; DFT calculation; INDUCED PASSIVITY-DEGRADATION; GENERATOR TUBING ALLOY; PROBE FORCE MICROSCOPY; ELECTRON WORK FUNCTION; POTENTIAL-PH DIAGRAMS; HIGH-TEMPERATURE; CAUSTIC SOLUTION; IN-SITU; BEHAVIOR; CRACKING;
D O I：
10.1016/j.corsci.2024.112469
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The vital role of hydrogen on lead-induced localized corrosion of Alloy 690TT in the simulated secondary crevice chemistries of pressurized water reactor at 25 degrees C is investigated by using surface analysis techniques and calculations. Density functional theory (DFT) calculation reveals that there is a coupling effect between lead and hydrogen on inhibiting the kinetic diffusion of oxygen vacancies. Experimental results show that hydrogen causes the change of most easily-corroded location from the grain/carbide interface to the TiN/nucleus interface in the lead-induced corrosion process, which provides a new interpreting sight as for lead-induced stress corrosion cracking mode of nickel-based Alloys.
引用
收藏
页数：13
相关论文
共 50 条
  • [21] Effects of Surface State and Applied Stress on Stress Corrosion Cracking of Alloy 690TT in Lead-containing Caustic Solution
    Zhiming Zhang
    JournalofMaterialsScience&Technology, 2012, 28 (09) : 785 - 792
  • [22] Lead-induced stress corrosion cracking behavior of mechanically surface-treated alloy 690
    Li, Nana
    Shi, San-Qiang
    Luo, Jingli
    Lu, Jian
    Wang, Ning
    MATERIALS RESEARCH LETTERS, 2016, 4 (03): : 180 - 184
  • [23] Mechanical polishing, surface roughness, near-surface deformation, and electrochemical corrosion of Alloy 690TT
    Arjmand, Farzin
    Zhang, Lefu
    SURFACE AND INTERFACE ANALYSIS, 2015, 47 (12) : 1120 - 1126
  • [24] Trans-twins stress corrosion cracking behaviors of Alloy 690TT in lead-containing caustic solution at 330 °C
    Zhang, Z. M.
    Wang, J. Q.
    Han, E. -H.
    Ke, W.
    NUCLEAR ENGINEERING AND DESIGN, 2011, 241 (12) : 4944 - 4952
  • [25] Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steelin Pure Water
    Xing-Chen Liu
    Hong-Liang Ming
    Zhi-Ming Zhang
    Jian-Qiu Wang
    Li-Chen Tang
    Hao Qian
    Yong-Cheng Xie
    En-Hou Han
    ActaMetallurgicaSinica(EnglishLetters), 2019, 32 (12) : 1437 - 1448
  • [26] Effect of mono-tension and biaxial tension on microstructure and stress corrosion cracking of Alloy 690TT
    Hou, J.
    Wang, J. Q.
    Ke, W.
    Han, E. H.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 518 (1-2): : 19 - 26
  • [27] Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steel in Pure Water
    Liu, Xing-Chen
    Ming, Hong-Liang
    Zhang, Zhi-Ming
    Wang, Jian-Qiu
    Tang, Li-Chen
    Qian, Hao
    Xie, Yong-Cheng
    Han, En-Hou
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2019, 32 (12) : 1437 - 1448
  • [28] The role of frequency on fretting corrosion of Alloy 690TT against 304 stainless steel in high temperature high pressure water
    Xin, L.
    Lu, Y. H.
    Otsuka, Y.
    Mutoh, Y.
    Wang, Z. H.
    Shoji, T.
    MATERIALS CHARACTERIZATION, 2017, 134 : 260 - 273
  • [29] Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steel in Pure Water
    Xing-Chen Liu
    Hong-Liang Ming
    Zhi-Ming Zhang
    Jian-Qiu Wang
    Li-Chen Tang
    Hao Qian
    Yong-Cheng Xie
    En-Hou Han
    Acta Metallurgica Sinica (English Letters), 2019, 32 : 1437 - 1448
  • [30] Microstructure and stress corrosion cracking behavior of Alloy 690TT steam generator tubes with internal bulge defect
    Wu, Bin
    Ming, Hongliang
    Zhang, Zhiming
    Meng, Fanjiang
    He, Guangqing
    Wang, Jianqiu
    Han, En-Hou
    JOURNAL OF NUCLEAR MATERIALS, 2022, 563
12345