Evaluation of the efficiency of Cr3+ → Cr4+ conversion in non-stoichiometric YAG: Cr ceramics

被引：2
|
作者：
Kravtsov, A. A. [1 ]
Suprunchuk, V. E. [1 ]
Lapin, V. A. [1 ]
Malyavin, F. F. [1 ]
Vakalov, D. S. [1 ]
Tarala, L. V. [1 ]
Medyanik, E. V. [1 ]
Brazhko, E. A. [1 ]
Chapura, O. M. [1 ]
Tarala, V. A. [1 ]
机构：
[1] North Caucasus Fed Univ, Pushkina St1, Stavropol 355009, Russia
来源：
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2024年 / 44卷 / 12期
关键词：
Ceramics; Stoichiometry; Valence conversion; Optical properties; YAG: Cr4+; OPTICAL-PROPERTIES; DEFECTS; IONS; CRYSTAL; STATE; LUMINESCENCE; DEVIATION;
D O I：
10.1016/j.jeurceramsoc.2024.04.078
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The aim of the work was to study the effect of the YAG: Cr ceramics' stoichiometry deviation on the optical properties and efficiency of valence conversion of Cr cations. YAG: Cr ceramic powders with deviations from stoichiometry ranging from 0.225 to -0.35 at % excess yttrium were synthesized by chemical precipitation. The optical and luminescent properties of YAG: Cr4+ ceramics, as well as the microstructure of the ceramics, were studied. It has been shown that small deviations from the stoichiometry of YAG: Cr (within 0.35 at %) do not have a significant effect on the optical transmission and microstructure of YAG: Cr3+ ceramics, but strongly affect some characteristics of YAG: Cr4+ ceramics. It was found that the presence of excess aluminum or yttrium cations in YAG: Cr4+ ceramics leads to a decrease in the concentration of Cr4+ and a deterioration in the conversion from Cr3+ to Cr4+.
引用
收藏
页码：7160 / 7169
页数：10
相关论文
共 50 条
  • [31] Performance of diode-end-pumped Cr4+, Nd3+ :YAG self Q switched and Nd:YAG/Cr4+:YAG diffusion bonded lasers
    Kalisky, Y
    Kravchik, L
    LASER CRYSTALS, GLASSES, AND NONLINEAR MATERIALS GROWTH AND CHARACTERIZATION, 2003, 4970 : 35 - 44
  • [32] 4.7 V Operation of the Cr4+/Cr3+ Redox Couple in Na3Cr2(PO4)2F3
    Kawai, Kosuke
    Asakura, Daisuke
    Nishimura, Shin-ichi
    Yamada, Atsuo
    CHEMISTRY OF MATERIALS, 2021, 33 (04) : 1373 - 1379
  • [33] Intensity-induced birefringence in Cr4+:YAG
    CamachoLopez, S
    Green, RPM
    Crofts, GJ
    Damzen, MJ
    JOURNAL OF MODERN OPTICS, 1997, 44 (01) : 209 - 219
  • [34] Effects of growth atmosphere, annealing temperature, Cr content, and Ca/Cr ratio on the Cr4+ absorption of Cr, Yb:YAG crystals
    Xu, XD
    Zhao, ZW
    Song, PX
    Zhou, GQ
    Xu, J
    Deng, PZ
    JOURNAL OF THE OPTICAL SOCIETY OF AMERICA B-OPTICAL PHYSICS, 2004, 21 (07) : 1289 - 1293
  • [35] Cr4＋：YAG激光器特性
    雷海容，张国威
    激光技术, 1996, (01) : 20 - 25
  • [36] Cr4+:YAG chirped-pulse oscillator
    Sorokin, Evgeni
    Kalashnikov, Vladimir L.
    Mandon, Julien
    Guelachvili, Guy
    Picque, Nathalie
    Sorokina, Irina T.
    NEW JOURNAL OF PHYSICS, 2008, 10
  • [37] Phase conjugation in Cr4+:YAG at 1.06 μm
    Opt Lett, 15 (1126):
  • [38] 连续Cr4+∶YAG激光器
    宋晏蓉
    张志刚
    裴为华
    宋丽军
    周国生
    中国激光, 2002, (03) : 204 - 204
  • [39] Absorption saturation mechanism for YAG:Cr4+ crystals
    Okhrimchuk, AG
    Shestakov, AV
    PHYSICAL REVIEW B, 2000, 61 (02): : 988 - 995
  • [40] Absorption of excited state of Cr4+:YAG crystal
    Leng, Y.X.
    Lin, L.H.
    Ouyang, B.
    Wan, X.K.
    Guangxue Xuebao/Acta Optica Sinica, 2001, 21 (02): : 225 - 227
12345