One-Step Synthesis of High-Efficiency Oxygen Evolution Reaction Catalyst FeSx(Y/MB) with High Temperature Resistance and Strong Alkali

Given the energy crisis and escalating environmental pollution, the imperative for developing clean new energy is evident. Hydrogen has garnered significant attention owing to its clean properties, high energy density, and ease of storage and transportation. This study synthesized four types of catalysts-FeS(DI/MB), FeS(ET/MB), Fe(DI/MB), and Fe(ET/MB)-using two distinct solution systems: DI/MB and ET/MB. The FeS(DI/MB) catalyst, synthesized using the layered solution system (DI/MB), demonstrates a uniformly distributed and dense nanosheet structure, exhibiting excellent resistance to strong bases and superior catalytic properties. The FeS(DI/MB) electrode showed OER overpotentials of 460 mV and 318 mV in 1 M and 6 M, respectively, at current densities of up to 500 mA cm(-2). Under industrial electrolysis test conditions, the FeS(DI/MB) electrode required only 262 mV to achieve a current density of 500 mA cm(-2), operating in a high-temperature, strong alkaline environment of 6 M at 60 degrees C. Furthermore, the FeS(DI/MB) electrode exhibited excellent OER catalytic activity and stability, as evidenced by a 60 h stability test These findings provide valuable insights into the preparation of iron nickel sulfide-based catalysts, and further in-depth and comprehensive exploration is anticipated to yield the excellent catalytic performance of these catalysts in the realm of electrolytic water hydrogen production.