Effect of Ultrasonic Rolling on Surface Properties of GCr15 Spherical Joint Bearing

被引:0
|
作者
Zhang, Hao [1 ]
Yang, Xiuli [2 ]
Ma, Xiqiang [1 ,3 ]
Jin, Dongliang [3 ,4 ]
You, Jinyuan [1 ]
机构
[1] Henan Univ Sci & Technol, Sch Mechatron Engn, Luoyang 471003, Peoples R China
[2] CCCC Second Harbour Engn Co Ltd, Wuhan 430040, Peoples R China
[3] Longmen Lab, Luoyang 471003, Peoples R China
[4] Natl Joint Engn Res Ctr Abras Control & Molding Me, Luoyang 471003, Peoples R China
关键词
ultrasonic rolling; surface roughness; surface hardness; friction coefficient; wear volume;
D O I
10.3390/lubricants12060208
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
Ultrasonic surface rolling process (USRP) has the potential to improve the surface mechanical properties of metal components with platelike or cylindrical macrostructure, but its effect on spherical surfaces remains to be studied in depth. In order to investigate the effect of USRP on the surface roughness, hardness and wear resistance of a spherical joint bearing made of GCr15 bearing steel, ultrasonic rolling strengthening was carried out on a spherical bearing surface under various conditions. The surface roughness and hardness variations of samples before and after strengthening were investigated. It was found that the USRP strengthening process can effectively enhance the surface properties of GCr15 spherical bearing materials, reduce the surface roughness by more than 45%, and increase the surface hardness by more than 10%. Friction and wear tests were carried out before and after ultrasonic rolling. The results show that the friction coefficient of the bearing surface can be reduced by 28%, and that the wear volume can be reduced by 29%. The variation in the friction coefficient correlated to the variance of wear volume as the reinforcement changes.
引用
收藏
页数:12
相关论文
共 50 条
  • [11] Strengthening Principle and Process Parameter Optimization of Ultrasonic Rolling of GCr15 Steel Bearing Roller
    Su, Chong
    Shi, Yansong
    Liu, Zheng
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (23) : 13079 - 13094
  • [12] Establishment of Surface Property Model and Optimization of Process Parameters for Ultrasonic Rolling GCr15
    Huang P.
    Wang Y.
    Cheng Y.
    Wang G.
    Yuan X.
    Surface Technology, 2024, 53 (05): : 156 - 165
  • [13] Effect of banded carbide structure on the rolling contact fatigue of GCr15 bearing steel
    Li, Ming
    Zhang, Henghua
    PROCEEDINGS OF THE 2017 5TH INTERNATIONAL CONFERENCE ON MECHATRONICS, MATERIALS, CHEMISTRY AND COMPUTER ENGINEERING (ICMMCCE 2017), 2017, 141 : 528 - 535
  • [14] Failure analysis for outer ring cracking of GCr15 rolling bearing
    Wang, Lan
    Qin, Peng
    Du, Zhe-tao
    Wu, Yao
    ENGINEERING FAILURE ANALYSIS, 2024, 157
  • [15] Effect of single/multi-particle grinding parameters on surface properties of bearing steel GCr15
    Hu, Lai
    Li, Banhu
    Pueh, Lee Heow
    Wang, Zixi
    Wang, Yuming
    ENGINEERING SCIENCE AND TECHNOLOGY-AN INTERNATIONAL JOURNAL-JESTECH, 2024, 58
  • [16] Laser Surface Hardening of GCr15 Bearing Steel Ring
    Akhter, R.
    Hussain, A.
    Farooq, W. A.
    Aslam, M.
    ADVANCED MATERIALS XI, 2010, 442 : 130 - 136
  • [17] Research on low temperature finish rolling of GCr15 bearing steel bar
    Liu, Jian-Heng
    Kang T'ieh/Iron and Steel (Peking), 2005, 40 (11): : 49 - 52
  • [18] Study on Rolling and Hot Delivery Spheroidizing Annealing of GCr15 Bearing Steel
    Huang, Zhi-Yuan
    Du, Lin-Xiu
    Li, Mu-Zi
    Fu, Si-Yu
    Lu, Jia-Ning
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (17) : 7779 - 7784
  • [19] Study on Rolling and Hot Delivery Spheroidizing Annealing of GCr15 Bearing Steel
    Zhi-Yuan Huang
    Lin-Xiu Du
    Mu-Zi Li
    Si-Yu Fu
    Jia-Ning Lu
    Journal of Materials Engineering and Performance, 2023, 32 : 7779 - 7784
  • [20] Effect of Cold Ring Rolling on the Wear Resistance of GCr15 Bearing Steel after Quenching and Tempering
    Lu, Bohan
    Wei, Wenting
    Mao, Huajie
    Lu, Xiaohui
    METALS, 2019, 9 (06)