Synthesis and physical characterization of novel Ag2 S-CdS /Ag /GNP ternary nanocomposite

A new type of Ag2S-CdS/Ag/GNP nanocomposite material was successfully synthesized in the presented work. The structural and physical properties of compounds were studied separately and together. Ag2S-CdS/Ag/GNP nanocomposite materials were studied by XRaman spectroscopy and Scanning Electron Microscopy (SEM). Based on the results, Ag nanowires (NWs) were successfully synthesized, and then it was determined that during the hybridization process, two phases of acanthite Ag2S and the cubic crystal system of Ag2O were formed. Then, Ag2S-CdS NWs were formed from mixed monoclinic Ag2S and hexagonal CdS. In the absorption spectrum of Ag NWs, the main absorbance peaks were observed at 357.3 nm and 380.2 nm. The energy gap (Eg) values of the Ag sample are 3.8 eV. The band gap value of Ag2S (2.5, 3.8, 4.6 eV) and Ag2S-CdS (2.5, 3.8, 4.8 eV) have a triple value due to the formation of a hybrid structure. The Raman spectrum of Ag2S-CdS belongs to longitudinal-optical (LO) phonon modes of zinc-blende phase CdS and for the 1, 2, and 3 times spin-coated samples on the surface of GNP/PVA have observed all characteristic Raman peaks, which belong to NWs at 485.13 cm-1, and 960.22 cm-1.