Effect of laser remelting scanning speed on microstructure and abrasion resistance of laser cladded Fe-based alloy coatings

被引：6

作者：

Deng, Rui ^{[1
]}

Mao, Muhua ^{[2
]}

Zhao, Chunjiang ^{[1
,3
]}

Ouyang, Changyao ^{[1
]}

Wei, Runze ^{[1
]}

Li, Huan ^{[1
]}

Liu, Haiyang ^{[4
]}

机构：

[1] Taiyuan Univ Sci & Technol, Sch Mech Engn, Taiyuan 030024, Peoples R China

[2] Ertuoqianqi Great Wall No 5 Min Co Ltd, Ertokqianqi 016200, Peoples R China

[3] Shanxi Inst Elect Technol, Sch Intelligent Ind, Linfen 041000, Peoples R China

[4] Shanxi Tangrong Machinery Mfg Co Ltd, Shuozhou 036000, Peoples R China

来源：

MATERIALS LETTERS | 2024年 / 366卷

基金：

中国国家自然科学基金;

关键词：

Additive manufacturing; Laser processing; Microstructure; Wear and tribology;

D O I：

10.1016/j.matlet.2024.136562

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this work, Fe -based alloy coatings were prepared on ductile iron substrates by laser cladding and laser remelting was used to further improve the abrasion resistance of the coatings. The result shows that increasing the remelting speed can gradually refine the microstructure and fully releases the residual stresses, and the interdendritic mesh structure becomes finer and denser. Compared with the original coating, remelted coatings have a significant increase in hardness and hardness uniformity. At the higher remelting speed of 40 mm/s, the coating had the highest hardness and abrasion resistance, 113.08 % and 157.55 % of the original coating, respectively.

引用

页数：5

共 50 条

[41] Effect of High-Speed Powder Feeding on Microstructure and Tribological Properties of Fe-Based Coatings by Laser Cladding
Wang, Qiang
Qian, Runling
Yang, Ju
Niu, Wenjuan
Zhou, Liucheng
Pan, Xinlei
Su, Chengming
COATINGS, 2021, 11 (12)
[42] Effects of scanning speed on microstructures and properties of laser cladding Fe-based amorphous composite coatings
Lu, Qinglong
Wang, Yanfang
Li, Li
Xiao, Lijun
Li, Xinmian
Yu, Zhiguo
Shi, Zhiqiang
Zhongguo Jiguang/Chinese Journal of Lasers, 2013, 40 (02):
[43] Effect of Heat Treatment on Mechanical and Anti-Corrosion Properties of Fe-Based Laser Cladded Coatings
Liu Shuang
Wang Qinying
Xi Yuchen
Tang Yirong
Pei Rui
Bai Shulin
LASER & OPTOELECTRONICS PROGRESS, 2019, 56 (12)
[44] Effect of La2O3 on microstructure and properties of Fe-based alloy coatings by laser cladding
Wang, Qiang
Yang, Ju
Niu, Wenjuan
Li, Yangyang
Mao, Xuan
Wang, Yonggang
Zhang, Kang
OPTIK, 2021, 245
[45] Effect of scanning speeds on solidification character and microstructure of co-based alloy in laser remelting
Zeng, Dawen
Xie, Changsheng
Jinshu Rechuli Xuebao/Transactions of Metal Heat Treatment, 1998, 19 (01): : 37 - 41
[46] Effects of Laser Oscillation Frequency on the Microstructure and Properties of TiC/Fe-Based Alloy Composite Coatings
Zhong, Yilan
Hu, Yongle
Zhang, Mingjun
Wang, Kaiming
Mao, Cong
Tang, Weidong
Pang, Xiaotong
Tong, Yonggang
Zhang, Yun
ADVANCED ENGINEERING MATERIALS, 2025, 27 (02)
[47] Effect of Scanning Speed on Properties of Laser Surface Remelting Layer of CuCr Alloy
Wang Xu
Yu Gang
He Xiuli
Li Shaoxia
Tian Chongxin
Shao Jiayun
Liu Baohua
LASER & OPTOELECTRONICS PROGRESS, 2022, 59 (01)
[48] Microstructure and properties of laser clad Fe-based amorphous alloy coatings containing Nb powder
Wang, Hao-Zheng
Cheng, Yan-Hai
Yang, Jing-Yong
Wang, Qing-Qing
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2020, 550
[49] Effect of the remelting scanning speed on the amorphous forming ability of Ni-based alloy using laser cladding plus a laser remelting process
Li, Ruifeng
Jin, Yajuan
Li, Zhuguo
Zhu, Yanyan
Wu, Mingfang
SURFACE & COATINGS TECHNOLOGY, 2014, 259 : 725 - 731
[50] Microstructure and Wear Resistance of Laser Cladded Coatings on Copper Substrate
Wang Wenyan
Lu Gao
Dong Xiao-ming
Xu Jing
Xie Jing-pei
ADVANCES IN MECHANICAL ENGINEERING, PTS 1-3, 2011, 52-54 : 1728 - 1731

← 1 2 3 4 5 →