Experimental Investigation of Phase Equilibria in the Al-Mo-Hf Ternary System at 400 °C and 600 °C

被引：0
|
作者：
Liu, Boliang [1 ]
Yu, Zhiqiang [1 ]
Liu, Libin [1 ]
Zhang, Ligang [1 ]
机构：
[1] Cent South Univ, Sch Mat Sci & Engn, Changsha 410083, Peoples R China
来源：
PROCESSES | 2024年 / 12卷 / 05期
基金：
中国国家自然科学基金;
关键词：
Al-Mo-Hf system; phase equilibrium; solid solubility; isothermal section; THERMODYNAMIC ASSESSMENT; CRYSTAL-STRUCTURE; ALUMINUM; HAFNIUM; ALLOYS; REFINEMENT; MOLYBDENUM; ZR;
D O I：
10.3390/pr12050969
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
This study investigates the phase equilibria of the Al-Mo-Hf ternary system at 400 degrees C and 600 degrees C using X-ray diffraction (XRD) and electron probe microanalysis (EPMA/WDS) techniques. Seven three-phase and five two-phase regions were identified at 400 degrees C, while eight three-phase and four two-phase regions were identified at 600 degrees C. Despite variations in the solid solubility ranges of certain compounds, the distribution of phase zones in the isothermal cross-section remained consistent at both temperatures. Using the experimental results and logical deductions, isothermal cross-sections were constructed for the Al-Mo-Hf ternary system at 600 degrees C and 400 degrees C.
引用
收藏
页数：17
相关论文
共 50 条
  • [41] Phase equilibria of the Al-Mn-Zn system at 600 °C
    Xu, Honghui
    Zhang, Fan
    Chen, Hai-Lin
    Xiong, Xiang
    Liang, J. L.
    Yin, Fucheng
    Du, Yong
    Jin, Zhanpeng
    JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 556 : 296 - 306
  • [42] Experimental investigation of phase equilibria in the Co-Fe-La system at 600 and 500 °C
    Fartushna, I
    Mardani, M.
    Khvan, A.
    Cheverikin, V
    Kondratiev, A.
    CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2020, 70
  • [43] Phase equilibria of the Al-Mn-Zn system at 600 °c
    Xu, H. (hhxu@csu.edu.cn), 1600, Elsevier Ltd (556):
  • [44] Experimental investigation of the phase equilibria of the La-Ti-Zn system at 600 and 450 °C
    Wu, Changjun
    Fan, Sailin
    Peng, Haoping
    Liu, Ya
    Wang, Jianhua
    Su, Xuping
    CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2018, 62 : 61 - 66
  • [45] Phase equilibria of the Al-Co-W system at 600 °C
    Liu, Ya
    Tang, Maoyou
    Zhang, Yifan
    Peng, Haoping
    Wang, Jianhua
    Su, Xuping
    JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 678 : 193 - 200
  • [46] INVESTIGATION OF MOLYBDENUM-RICH RANGE OF PHASE DIAGRAM OF TERNARY MO-HF-C SYSTEM
    ZAKHAROV, AM
    SAVITSKI.EM
    RUSSIAN METALLURGY-METALLY-USSR, 1969, (04): : 144 - &
  • [47] Solidification pathways and phase equilibria in the Mo-Ti-C ternary system
    Ida, Shuntaro
    Sekido, Nobuaki
    Yoshimi, Kyosuke
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2020, 39 (01) : 164 - 170
  • [48] Phase Equilibria of the Co-Mo-Zr Ternary System at 1100 °C
    Chaoying Lin
    Cong Zhang
    Shimin Wang
    Peng Zhou
    Yong Du
    Journal of Phase Equilibria and Diffusion, 2017, 38 : 552 - 560
  • [49] Phase Equilibria of the Co-Mo-Zr Ternary System at 1100 °C
    Lin, Chaoying
    Zhang, Cong
    Wang, Shimin
    Zhou, Peng
    Du, Yong
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2017, 38 (04) : 552 - 560
  • [50] Phase Equilibria of the Co-Mo-Zr Ternary System at 1000 °C
    Chaoying Lin
    Cong Zhang
    Shimin Wang
    Peng Zhou
    Yong Du
    Journal of Phase Equilibria and Diffusion, 2018, 39 : 510 - 518
12345