Physical and thermomechanical characterization of unidirectional Helicteres isora fiber-reinforced polylactic acid bio-composites

Identifying novel cellulose fiber bio-composites has become a vital initiative in the exploration of sustainable materials due to increased global concern for the environment. This growing focus on eco-friendly materials has gathered significant attention in recent years. The current investigation deals with one such material, Helicteres isora reinforced Polylactic acid composites. Surface chemical treatment of fiber is one of the most effective methods to modify the hydrophilic fiber to increase its compatibility with the polymer matrix. Sodium hydroxide was used as a pre-treatment chemical to remove any impurities from the fiber surface. Pre-treated fibers were treated with Methacryl silane and Potassium permanganate solution to chemically modify the fiber surface. Density, void content and water absorption behavior of the composites were analyzed as per the standard procedure. Tensile and flexural tests were conducted to evaluate the mechanical strength, modulus, and flexibility of the unidirectional composites. Thermogravimetric and differential thermal analyses were performed to investigate the thermal stability, melting behavior and degradation profiles of prepared composites. A study of failure mechanisms and morphology of the fractured surface through photographs and SEM images revealed fiber splitting and delamination as the dominant reasons behind the failure of composites under tensile loading. Silane-treated Helicteres isora fiber-reinforced Polylactic acid composite exhibited lower water absorption and higher tensile strength than its counterparts. Untreated fiber composite showed maximum flexural strength among the tested composites. By collectively evaluating the results of the tests and properties of the composites, silane-treated fiber-reinforced Polylactic acid composites stands out as the most favorable choice.