Preparation and regeneration performance of modified semi-carbon for flue gas SO2 adsorbent

被引：0

作者：

Liu J.-J. ^{[1
,2
]}

Su W. ^{[1
,3
]}

Xing Y. ^{[1
,3
]}

Liu W.-M. ^{[4
]}

Zhao Q.-T. ^{[2
]}

Pang S.-G. ^{[2
]}

Jiang S. ^{[2
]}

Wei X.-M. ^{[2
]}

Li X.-Y. ^{[1
]}

机构：

[1] School of Energy and Environmental Engineering, Beijing University of Science and Technology, Beijing

[2] China North Energy Conservation and Environment Protection Co., Ltd., Beijing

[3] Beijing Key Laboratory of Resource-oriented Treatment of Industrial Pollutants, Beijing

[4] State Key Laboratory Solid Waste Reuse for Building Materials, Beijing Building Materials Academy of Sciences Research, Beijing

来源：

Gongcheng Kexue Xuebao/Chinese Journal of Engineering | 2021年 / 43卷 / 02期

关键词：

Activation; Adsorbents; Flue gas purification; Regeneration; Semi-coke;

D O I：

10.13374/j.issn2095-9389.2020.02.21.001

中图分类号：

学科分类号：

摘要：

The use of adsorbents such as activated coke to separate pollutants from flue gas is an effective flue gas treatment method. As a cheap carbon material, semi-carbon is a potential porous alternative material to the existing commercial activated coke. In this work, the effects of the carbonization time, carbonization temperature, and binder addition on the properties of prepared adsorbents from Shanxi semi-coke were studied. The microstructure changes were investigated, and the changes in the surface functional groups in the adsorption and desorption process were explored via X-ray photoelectron spectroscopy (XPS). The results show that the carbonization temperature has a significant effect on the wear resistance and compressive strength index, and the carbonization time has a significant effect on the saturated desulfurization value and the breakthrough desulfurization value. In addition, under the conditions of 50% coal tar addition ratio, 700 ℃ carbonization for 20 min, and 900 ℃ activation for 60 min, the modified semi-coke parameters were as follows: abrasion resistance 95.81%, compressive strength 536.1 N·cm−1, saturated desulfurization value per g of semi-carbon is 45.71 mg, and breakthrough desulfurization value per g of semi-carbon is 23.45 mg. When the first failure occurred in the adsorbents after 10 thermal regeneration processes, the activated carbon surface was etched over a large area with severe changes in the surface morphology under the above conditions. Some large granular activated carbons were etched and pulverized into small particles. The activated carbon surface structure was also etched out of pores, which may be caused by the C consumption resulting from the interaction of C and H2SO4. The results also show that the secondary activation could increase the adsorption capacity in a short time, but the activated carbon performance degradation is also significant. The amount and composition ratio of the oxygen-containing groups on the surface of the modified semi-coke affected the adsorption performance. The ratio of oxygen to carbon groups corresponded to the adsorption performance: the higher the proportion of oxygen-containing groups, the worse the adsorption performance. The proportion of oxygen-containing groups was changed by the second activation regeneration, and C=O decreased significantly, O−C=O increased significantly, while C−O changed slightly. Although the O−C=O functional group contains oxygen, it may not significantly inhibit adsorption. This study provides a new adsorbent-preparation method for industrial flue gas treatment and also provides a reference for the research on the surface modification of semi-coke and the adsorption and desorption mechanisms of sulfur dioxide. Copyright ©2021 Chinese Journal of Engineering. All rights reserved.

引用

页码：223 / 231

页数：8

共 33 条

[11] Zhao J X, Li H J, Li X M, Et al., Technical progress and analysis of semi-coke production with low metamorphic degree coal, Clean Coal Technol, 16, 6, (2010)
[12] Zhang Y, Lan X Z, Song Y H., Research progress of removal SO2 from flue gas using modified semi-coke, Clean Coal Technol, 14, 1, (2008)
[13] Bhatnagar A, Hogland W, Marques M, Et al., An overview of the modification methods of activated carbon for its water treatment applications, Chem Eng J, 219, (2013)
[14] Li Y S, Xu G Z, Li B B, Et al., Preparation of micro-pore dominated active carbon powder by using semi-coke powder activated with CO2, J Univ Sci Technol Liaoning, 41, 6, (2018)
[15] Liu C B, Lan X Z, Tian Y H, Et al., Influence of carbonization temperature on the performance of formed activated carbon based on blue-coke, Coal Convers, 35, 1, (2012)
[16] Zhang S Y, Wang Y, Zhu T Y, Et al., The effects of activation conditions on the porous texture of activated char derived from Binxian Coal, Chem React Eng Technol, 19, 3, (2003)
[17] Liu Y S, Wang H H, Zhang H, Et al., Experimental study on catalytic reaction rate of activated carbon flue gas desulfurization, J Beijing Univ Sci Technol, 36, 2, (2014)
[18] Chen K H, Song C Y, Qiu L, Et al., Removal of SO2 from flue gas by fluidized activated carbon fiber, J Beijing Univ Sci Technol, 31, 3, (2009)
[19] Liu J J, Song C Y, Tong Z S, Et al., Study on thermal regeneration performance of activated carbon for desulfurization, Environ Eng, 36, (2018)
[20] Davini P., Adsorption and desorption of SO2 on active carbon: The effect of surface basic groups, Carbon, 28, 4, (1990)

← 1 2 3 4 →