Optimized Synthesis of Carbon Aerogels via Ambient Pressure Drying Process as Electrode for Supercapacitors

被引：0

作者：

袁磊 ^{[1
]}

CHANG Lijuan ^{[2
]}

FU Zhibing ^{[1
]}

YANG Xi ^{[1
]}

JIAO Xingli ^{[1
]}

TANG Yongjian ^{[1
]}

LIU Xichuan ^{[3
]}

王朝阳 ^{[1
]}

机构：

[1] Science and Technology on Plasma Physics Laboratory, Research Centre of Laser Fusion, China Academy of Engineering Physics

[2] Institute of Atomic and Molecular Physics, Sichuan University

[3] College of Material Science and Engineering, Xihua

来源：

Journal of Wuhan University of Technology(Materials Science Edition) | 2015年 / 30卷 / 06期

关键词：

D O I：

暂无

中图分类号：

TQ427.26 []; TM53 [电容器];

学科分类号：

摘要：

Carbon aerogels were synthesized via ambient pressure drying process using resorcinolformaldehyde as precursor and P123 to strengthen their skeletons. CO2 activation technology was implemented to improve surface areas and adjust pore size distribution. The synthesis process was optimized, and the morphology, structure, adsorption properties and electrochemical behavior of different samples were characterized. The CO2-activated samples achieved a high specific capacitance of 129.2 F/g in 6 M KOH electrolytes at the current density of 1 m A/cm2 within the voltage range of 0-0.8 V. The optimized activation temperature and duration were determined to be 950 ℃ and 4 h, respectively.

引用

页码：1325 / 1331

页数：7

共 50 条

[41] Synthesis of silica aerogels from waterglass via new modified ambient drying
Lee, CJ
Kim, GS
Hyun, SH
JOURNAL OF MATERIALS SCIENCE, 2002, 37 (11) : 2237 - 2241
[42] Preparation and properties of silica aerogels reinforced using polyurethanes via ambient pressure drying
School of Materials Science and Engineering, Tianjin Chengjian University, Tianjin, China
Rengong Jingti Xuebao, 12 (3532-3536):
[43] Synthesis of low shrinkage monolith alumina aerogels by surface modification and ambient pressure drying
Li, Chi
Gong, Zheng
Ding, Likang
Guo, Donglai
Hu, Wenbin
MICRO & NANO LETTERS, 2018, 13 (09): : 1240 - 1244
[44] Carbon aerogels as electrode material for electrical double layer supercapacitors-Synthesis and properties
Halama, Agnieszka
Szubzda, Bronislaw
Pasciak, Grzegorz
ELECTROCHIMICA ACTA, 2010, 55 (25) : 7501 - 7505
[45] Ionothermal synthesis of microporous and mesoporous carbon aerogels from fructose as electrode materials for supercapacitors
Lin, Xiao-Xiao
Tan, Bin
Peng, Lu
Wu, Zhao-Feng
Xie, Zai-Lai
JOURNAL OF MATERIALS CHEMISTRY A, 2016, 4 (12) : 4497 - 4505
[46] Preparation of mesoporous carbon aerogels via ambient pressure drying using a self-sacrificing melamine-formaldehyde template
Yang, Xiaoqing
Yang, Dan
Zhang, Guoqing
Zuo, Huajiang
JOURNAL OF POWER SOURCES, 2021, 482
[47] Mesoporous aerogels synthesized with an ionic liquid [Hmim]Br as template via ambient pressure drying
Dai, Hongyi
Yan, Hairui
Yu, Chunling
Fu, Yinghuan
Shao, Guolin
Ning, Liyuan
Wu, Xuyang
SUSTAINABLE DEVELOPMENT OF NATURAL RESOURCES, PTS 1-3, 2013, 616-618 : 1864 - 1868
[48] Rapid Fabrication of Monolithic Carbon Aerogels Based on Resorcinol-Formaldehyde by Ambient Pressure Drying
Park, Seung-Kyu
Kim, Heon-Chang
Oh, Chang-Sup
Kim, Yong-Ha
ASIAN JOURNAL OF CHEMISTRY, 2013, 25 (10) : 5395 - 5398
[49] Preparation and Heat Treatment of Titania Aerogels by Ambient Pressure Drying
Guo Xingzhong
Sun Sai
Li Wenyan
Shen Qianhong
RARE METAL MATERIALS AND ENGINEERING, 2012, 41 : 475 - 478
[50] Solvent Cavitation during Ambient Pressure Drying of Silica Aerogels
Gonthier, Julien
Scoppola, Ernesto
Rilling, Tilman
Gurlo, Aleksander
Fratzl, Peter
Wagermaier, Wolfgang
LANGMUIR, 2024, 40 (25) : 12925 - 12938

← 1 2 3 4 5 →