Low Sm Doping Effects on the Low-Field Magnetoresistive Properties in (La1-xSmx)(0.67)Sr0.33MnO3 Perovskite

A series of polycrystalline samples (La1-xSmx)(0.67)Sr0.33MnO3 (X=0.00, 0.05 and 0.10) were prepared using the conventional solid-state reaction method. The XRD analysis indicated that all the samples were fully crystalline and in a single phase with a rhombohedral structure after a sintering at I200 degrees C for 24 hours in air. Meanwhile, the Atomic Force Microscopy measurements showed that a small amount of Sm doping in La sites affected the grain growth and this might affect the grain boundary layer, thus resulting in the reduction of the Curie temperature, T-C.( )Extrinsic magnetoresistance (MR) was observed for all the samples with a large negative MR at low field (0-0.1 or 0.2T) region, followed by a slower varying MR at high field (0.1 or 0.2-1T). The highest low-field MR value of -4.6% (at 0.1T) and -6.1% (at 0.2T) were observed for sample X=0.10 and X=0.05, respectively. Hence, these indicated that the extrinsic MR was grain size dependent and was therefore enhanced with a small amount of Sm substitution in La sites.