FRACTURE-TOUGHNESS OF YBA2CU3OX CONTAINING Y2BACUO5 AND ZRO2

被引：18

作者：

GORETTA, KC ^{[1
]}

KULLBERG, ML ^{[1
]}

BAR, D ^{[1
]}

RISCH, GA ^{[1
]}

ROUTBORT, JL ^{[1
]}

机构：

[1] ARGONNE NATL LAB,DIV MAT SCI,ARGONNE,IL 60439

来源：

SUPERCONDUCTOR SCIENCE & TECHNOLOGY | 1991年 / 4卷 / 10期

关键词：

D O I：

10.1088/0953-2048/4/10/006

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Tetragonal ZrO2 particles have been added to superconducting YBa2Cu3Ox (123) to improve its fracture toughness (K(IC)). Reactions between the ZrO2 and 123 prevented the ZrO2 from providing significant toughening. A sol-gel coating of Y2BaCuO5 (211) on the ZrO2 particles minimized the deleterious reactions. Addition of 20 mol% ZrO2 coated with 211 yielded a 123 composite with a K(IC) of 4.5 MPa m0.5.

引用

页码：544 / 547

页数：4

共 50 条

[21] The influence of the starting YBa2Cu3Ox powder on the microstructure of melt-textured YBa2Cu3O7-x/Y2BaCuO5 bulks
Kracunovska, S
Diko, P
Litzkendorf, D
Habisreuther, T
Gawalek, W
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 397 (3-4): : 123 - 131
[22] Fine Y2BaCuO5 particles in fluorine-doped YBa2Cu3Ox superconductors synthesized at temperatures below 950 °C
Miyakonojo Natl Coll of Technology, Miyazaki, Japan
Mater Chem Phys, 3 (246-252):
[23] INFLUENCES OF Y2BACUO5 PARTICLE-SIZE AND CONTENT ON THE TRANSPORT CRITICAL CURRENT-DENSITY OF YBA2CU3OX SUPERCONDUCTOR
LEE, DF
SELVAMANICKAM, V
SALAMA, K
PHYSICA C, 1992, 202 (1-2): : 83 - 96
[24] Fine Y2BaCuO5 particles in fluorine-doped YBa2Cu3Ox superconductors synthesized at temperatures below 950°C
Hamada, T
Morimo, R
Ohzono, Y
Tanaka, K
MATERIALS CHEMISTRY AND PHYSICS, 1998, 52 (03) : 246 - 252
[25] TEM AND CRITICAL-CURRENT DENSITY STUDIES OF MELT-TEXTURED YBA2CU3OX WITH SILVER AND Y2BACUO5 ADDITIONS
MIRONOVA, M
LEE, DF
SALAMA, K
PHYSICA C, 1993, 211 (1-2): : 188 - 204
[26] ANALYSIS OF THE STABILITY OF YBA2CU3OX (X=6.5-7.0, T=298-1200K) TO DECOMPOSITION INTO Y2BACUO5, BACUO2, AND CUO
SANYGIN, VP
SHEBERSHNEVA, OV
LAZAREV, VB
INORGANIC MATERIALS, 1994, 30 (11) : 1370 - 1375
[27] IRON SUBSTITUTION IN Y2BACUO5 AND YBA2CU3O7-Y
DEMARCO, M
TRBOVICH, G
WANG, XW
HAO, J
NAUGHTON, M
WHITE, M
JOURNAL OF APPLIED PHYSICS, 1991, 69 (08) : 4886 - 4888
[28] I–V characteristics and the electric-field effect in melt-grown YBa2Cu3Ox/Y2BaCuO5 HTSC crystals
B. I. Smirnov
T. S. Orlova
S. Sengupta
K. C. Goretta
Physics of the Solid State, 2000, 42 : 1207 - 1210
[29] Vortex liquid in YBa2Cu3O7:Y2BaCuO5
Galante, F
Rodriguez, E
Fontcuberta, J
Obradors, X
PHYSICA C, 1998, 296 (1-2): : 96 - 102
[30] THERMODYNAMIC FUNCTIONS OF YBA2CU3O7, YBA2CU3O6, Y2BACUO5 AND BACUO2
TSAGAREISHVILI, DS
GVELESIANI, GG
BARATASHVILI, IB
MOISEEV, GK
VATOLIN, NA
ZHURNAL FIZICHESKOI KHIMII, 1990, 64 (10): : 2606 - 2610

← 1 2 3 4 5 →