CHROME-MANGANESE AUSTENITIC STEELS RESISTANT TO STRESS CORROSION CRACKING IN SOLUTIONS OF MAGNESIUM AND CALCIUM CHLORIDES

被引：2

|

作者：

CIHAL, V

POBORIL, F

机构：

来源：

REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES | 1969年 / 66卷 / 03期

关键词：

D O I：

10.1051/metal/196966030199

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

引用

收藏

页码：199 / +

相关论文

共 50 条

[31] Effects of potential and stress corrosion cracking of austenitic stainless steels in concentrated chloride solutions
Jiang, XC
Staehle, RW
CORROSION, 1997, 53 (08) : 631 - 643
[32] Localized corrosion and stress corrosion cracking of stainless steels in halides other than chlorides solutions: a review
Kappes, Mariano A.
CORROSION REVIEWS, 2020, 38 (01) : 1 - 24
[33] INVESTIGATIONS INTO TRANSGRANULAR AND INTERGRANULAR STRESS-CORROSION CRACKING OF AUSTENITIC STAINLESS-STEELS IN HOT MAGNESIUM-CHLORIDE SOLUTIONS
KESSLER, KJ
KAESCHE, H
WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1984, 35 (05): : 171 - 178
[34] Stress corrosion cracking and life prediction evaluation of austenitic stainless steels in calcium chloride solution
Leinonen, H
CORROSION, 1996, 52 (05) : 337 - 346
[35] THERMOMECHANICAL EFFECTS ON STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS
BATES, JF
MATERIALS PROTECTION AND PERFORMANCE, 1970, 9 (10): : 27 - &
[36] MECHANISM OF CHLORIDE STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS
RHODES, PR
CORROSION, 1969, 25 (11) : 462 - &
[37] Role of hydrogen in stress corrosion cracking of austenitic stainless steels
Lu, B. T.
Qiao, L. J.
Luo, J. L.
Gao, K. W.
PHILOSOPHICAL MAGAZINE, 2011, 91 (02) : 215 - 235
[38] THERMOMECHANICAL EFFECTS ON STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS
BATES, JF
MATERIALS PROTECTION, 1969, 8 (12): : 35 - &
[39] Marine atmospheric stress corrosion cracking of austenitic stainless steels
Kain, Robert M.
Materials Performance, 1990, 29 (12) : 60 - 62
[40] INITIAL STAGES OF STRESS CORROSION CRACKING IN AUSTENITIC STAINLESS STEELS
LOUTHAN, MR
CORROSION, 1965, 21 (09) : 288 - &

← 1 2 3 4 5 →