High-Energy-Density Cathode Achieved via the Activation of a Three-Electron Reaction in Sodium Manganese Vanadium Phosphate for Sodium-Ion Batteries

Sodium superionic conductor (NASICON)-type Na3V2(PO4)(3) has attracted considerable interest owing to its stable three-dimensional framework and high operating voltage; however, it suffers from a low-energy density due to the poor intrinsic electronic conductivity and limited redox couples. Herein, the partial substitution of Mn3+ for V3+ in Na3V2(PO4)(3) is proposed to activate V4+/V5+ redox couple for boosting energy density of the cathodes (Na3V2-xMnx(PO4)(3)). With the introduction of Mn3+ into Na3V2(PO4)(3), the band gap is significantly reduced by 1.406 eV and thus the electronic conductivity is greatly enhanced. The successive conversions of four stable oxidation states (V2+/V3+, V3+/V4+, and V4+/V5+) are also successfully achieved in the voltage window of 1.4-4.0 V, corresponding to three electrons involved in the reversible reaction. Consequently, the cathode with x = 0.5 exhibits a high reversible discharge capacity of 170.9 mAh g(-1) at 0.5 C with an ultrahigh energy density of 577 Wh kg(-1). Ex-situ x-ray diffraction (XRD) analysis reveals that the sodium-storage mechanism for Mn-doped Na3V2(PO4)(3) consists of single-phase and bi-phase reactions. This work deepens the understanding of the activation of reversible three-electron reaction in NASICON-structured polyanionic phosphates and provides a feasible strategy to develop high-energy-density cathodes for sodium-ion batteries.