STRESS-CORROSION CRACKING BEHAVIOR OF 2 HIGH-STRENGTH AL-XCU-LI-AG-MG-ZR ALLOYS

被引：1
|
作者：
MOSHIER, WC
SHAW, BA
TACK, WT
PHULL, B
机构：
[1] PENN STATE UNIV,UNIV PK,PA 19104
[2] LAQUE CTR CORROS TECHNOL,WRIGHTSVILLE BEACH,NC 28480
来源：
CORROSION | 1992年 / 48卷 / 04期
关键词：
AL-LI ALLOYS; HIGH-STRENGTH ALUMINUM ALLOYS; SLOW STRAIN RATE TESTING; STRESS CORROSION CRACKING;
D O I：
10.5006/1.3315936
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The rapid drop-off of the ductility ratio for Alloy 1 and its subsequent partial recovery and the evidence of intersubgranular attack suggest that SCC plays a role in its failure. The results for Alloy 2 are less clear, and pitting may significantly contribute to failure. The contribution of pitting attack in these alloys cannot be ignored, and standard SCC testing of Weldalite 049 for extended exposure times could lead to erroneous results based on pitting-controlled fracture rather than actual SCC susceptibility.
引用
收藏
页码：306 / 308
页数：3
相关论文
共 50 条
  • [1] Stress corrosion cracking behavior of Al−Cu−Li−Mg−Zr(−Ag) alloys
    Chang-Soon Lee
    Yong Choi
    In Gyu Park
    Metals and Materials International, 2002, 8 : 191 - 196
  • [2] Stress corrosion cracking behavior of Al-Cu-Li-Mg-Zr(-Ag) alloys
    Lee, Chang-Soon
    Choi, Yong
    Park, In Gyu
    Metals and Materials International, 2002, 8 (02): : 191 - 196
  • [3] Stress corrosion cracking behavior of Al-Cu-Li-Mg-Zr(-Ag) alloys
    Lee, CS
    Choi, Y
    Park, IG
    METALS AND MATERIALS INTERNATIONAL, 2002, 8 (02) : 191 - 196
  • [4] STRESS-CORROSION CRACKING OF AL-LI-ZR ALLOYS
    CHRISTODOULOU, L
    TOESCA, S
    PICKENS, JR
    JOURNAL OF METALS, 1984, 36 (07): : 44 - 44
  • [5] A NEW STRESS-CORROSION CRACKING TEST FOR HIGH-STRENGTH ALLOYS
    BROWN, BF
    MATERIALS RESEARCH AND STANDARDS, 1966, 6 (03): : 129 - &
  • [6] STRESS-CORROSION CRACKING OF HIGH-STRENGTH ALUMINUM-ALLOYS
    GRUHL, W
    ZEITSCHRIFT FUR METALLKUNDE, 1984, 75 (11): : 819 - 826
  • [7] STRESS-CORROSION CRACKING BEHAVIOR OF HIGH-STRENGTH ALUMINUM POWDER METALLURGY ALLOYS.
    Pickens, J.R.
    Christodoulou, L.
    1600, (18 A):
  • [8] THE STRESS-CORROSION CRACKING BEHAVIOR OF HIGH-STRENGTH ALUMINUM POWDER-METALLURGY ALLOYS
    PICKENS, JR
    CHRISTODOULOU, L
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (01): : 135 - 149
  • [9] STRESS-CORROSION CRACKING OF HIGH-STRENGTH STEELS AND TITANIUM-ALLOYS
    JUDY, RW
    GOODE, RJ
    WELDING JOURNAL, 1972, 51 (09) : S437 - &
  • [10] STRESS-CORROSION CRACKING OF HIGH-STRENGTH STEELS AND TITANIUM-ALLOYS
    JUDY, RW
    GOODE, RJ
    REPORT OF NRL PROGRESS, 1972, (JAN): : 21 - &
12345