STUDY OF FATIGUE CRACK INITIATION ON HIGH-STRENGTH STEEL SPECIMENS HAVING SHAPE DEFECTS AND DIFFERENT DIMENSIONS

被引：0
|
作者：
BAUS, A [1 ]
LIEURADE, HP [1 ]
SANZ, G [1 ]
TRUCHON, M [1 ]
机构：
[1] IRSID,ST GERMAIN EN LAYE,FRANCE
来源：
REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES | 1977年 / 74卷 / 10期
关键词：
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
引用
收藏
页码：565 / 584
页数：20
相关论文
共 50 条
  • [1] INITIATION AND PROPAGATION OF FATIGUE CRACK IN HIGH-STRENGTH EUTECTOID STEEL
    YOKOBORI, T
    SAWAKI, Y
    SHONO, S
    KUMAGAI, A
    [J]. TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1976, 17 (01): : 1 - 10
  • [2] Crack initiation characteristics and fatigue property of a high-strength steel in VHCF regime under different stress ratios
    Liu, Xiaolong
    Sun, Chengqi
    Hong, Youshi
    [J]. FRATTURA ED INTEGRITA STRUTTURALE, 2016, (35): : 88 - 97
  • [3] Crack Initiation and Propagation Fatigue Life of Ultra High-Strength Steel Butt Joints
    Ottersboeck, Markus J.
    Leitner, Martin
    Stoschka, Michael
    Maurer, Wilhelm
    [J]. APPLIED SCIENCES-BASEL, 2019, 9 (21):
  • [4] Fatigue crack initiation site transition of high-strength steel under very high-cycle fatigue
    Teng, Xiaoyuan
    Pang, Jianchao
    Gao, Chong
    Li, Shouxin
    Zhang, Zhefeng
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, : 4450 - 4464
  • [5] Experimental Study on Fatigue Crack Propagation of High-Strength Steel Wire with Initial Defects for Bridge Cables
    Wang, Ying
    Zhang, Wenhui
    Pan, Xu
    Zheng, Yuqian
    [J]. APPLIED SCIENCES-BASEL, 2020, 10 (12):
  • [6] FATIGUE CRACK RETARDATION OF HIGH-STRENGTH STEEL IN SALTWATER
    TOKAJI, K
    ANDO, Z
    IMAI, T
    KOJIMA, T
    [J]. JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1983, 105 (02): : 88 - 92
  • [7] High-cycle fatigue crack initiation and propagation behaviour of high-strength spring steel wires
    Wang, QY
    Berard, JY
    Rathery, S
    Bathias, C
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1999, 22 (08) : 673 - 677
  • [8] Subsurface crack initiation and propagation mechanism in high-strength steel in a very high cycle fatigue regime
    Shiozawa, K.
    Morii, Y.
    Nishino, S.
    Lu, L.
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2006, 28 (11) : 1521 - 1532
  • [9] FATIGUE CRACK INITIATION AND FATIGUE LIFE TESTING OF HIGH-STRENGTH AUSTENITIC STAINLESS STEEL TUBING WITH INTERNAL HYDROGEN
    San Marchi, Chris
    Ronevich, Joseph A.
    Pohl, Johan
    Ramseyer, Severin
    Cortinovis, Davide
    Eckmann, Stefan
    [J]. PROCEEDINGS OF ASME 2023 PRESSURE VESSELS & PIPING CONFERENCE, PVP2023, VOL 5, 2023,
  • [10] Very high cycle fatigue of high-strength steels: Crack initiation by FGA formation investigated at artificial defects
    Spriestersbach, D.
    Brodyanski, A.
    Loesch, J.
    Kopnarski, M.
    Kerscher, E.
    [J]. 21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21), 2016, 2 : 1101 - 1108
12345