THERMODYNAMIC ASPECTS OF TIAL AND TISI2 OXIDATION - THE AL-TI-O AND SI-TI-O PHASE-DIAGRAMS

被引：256

作者：

RAHMEL, A ^{[1
]}

SPENCER, PJ ^{[1
]}

机构：

[1] RHEIN WESTFAL TH AACHEN,LEHRSTUHL THEORET HUTTENKUNDE & MET KERNBRENNSTOFFE,W-5100 AACHEN,GERMANY

来源：

OXIDATION OF METALS | 1991年 / 35卷 / 1-2期

关键词：

METAL ACTIVITY VARIATION; TI-AL SYSTEM; TI-SI SYSTEM; TI-AL-O PHASE DIAGRAM; TI-SI-O PHASE DIAGRAM;

D O I：

10.1007/BF00666500

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Thermodynamic data from the literature were used to calculate the activity variations of Ti and Al in the Ti-Al system at 700, 900, and 1100-degrees-C and of Ti and Si in the Ti-Si system at 800, 1000, and 1300-degrees-C. The activity data were then applied to estimate the stable oxide phase in equilibrium with the metal phase, assuming that the activity of the oxide phase was unity. It was found that in the Ti-Al-O system the stable oxide changed from TiO to Al2O3 in the existence region of the TiAl phase, while in the Ti-Si-O system a comparable change from Ti-oxide to SiO2 occurred in the existence region of the Ti5Si3 phase. The significance of these results to the oxidation of intermetallics in the Ti-Al and Ti-Si systems is discussed briefly.

引用

页码：53 / 68

页数：16

共 50 条

[41] LUMINESCENCE AND COLOR-CENTERS IN AL2O3-SI,TI
MEHTA, SK
SENGUPTA, S
NUCLEAR INSTRUMENTS & METHODS, 1979, 164 (02): : 349 - 354
[42] PHASE-EQUILIBRIA IN THE TI-AL-O SYSTEM AT 945-DEGREES-C AND ANALYSIS OF TI/AL2O3 REACTIONS
KELKAR, GP
CARIM, AH
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1995, 78 (03) : 572 - 576
[43] ENVIRONMENTAL DOSIMETRY WITH AL2O3(SI,TI) THERMOLUMINESCENT PHOSPHOR
MEHTA, SK
SENGUPTA, S
OOMMEN, IK
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH, 1982, 197 (2-3): : 459 - 463
[44] Characterization and mechanical testing on novel (γ + α2 ) - TiAl/Ti3Al/Al2O3 cermet
Li, H. Y.
Motamedi, P.
Hogan, J. D.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 750 : 152 - 163
[45] THE TERNARY-SYSTEMS CU-TI-AL AND CU-ZR-AL AROUND THE HEUSLER PHASE-COMPOSITION CU2TIAL, CU2ZRAL - PHASE-DIAGRAMS AND HYDROGEN SOLUBILITY
RECKENDORF, RMZ
SCHMIDT, PC
WEISS, A
JOURNAL OF THE LESS-COMMON METALS, 1990, 159 (1-2): : 277 - 289
[46] HIGH-TEMPERATURE OXIDATION OF 2-PHASE (TI3AL + TIAL) INTERMETALLIC COMPOUNDS
TAKASAKI, A
OJIMA, K
TANEDA, Y
HOSHIYA, T
MITSUHASHI, A
SCRIPTA METALLURGICA ET MATERIALIA, 1992, 27 (04): : 401 - 405
[47] Nanoprecipitation in Al2O3 3 mol%Ti2O3 due to oxidation
Yasuda, A
Aoki, J
Sakuma, T
CERAMICS INTERNATIONAL, 1998, 24 (07) : 483 - 487
[48] A GENERAL CHEMOGRAPHIC APPROACH TO THE CONSTRUCTION OF TERNARY PHASE-DIAGRAMS, WITH APPLICATION TO THE SYSTEM AL2O3-SIO2-H2O
STOUT, JH
AMERICAN JOURNAL OF SCIENCE, 1985, 285 (05) : 385 - 408
[49] Al6Ti2O13, a new phase in the Al2O3-TiO2 system
Norberg, ST
Hoffmann, S
Yoshimura, M
Ishizawa, N
ACTA CRYSTALLOGRAPHICA SECTION C-STRUCTURAL CHEMISTRY, 2005, 61 : I35 - I38
[50] Effect of Sintering Temperature on Al2O3/TiAl Composite from Ti-Al-TiO2-Eu2O3 System
Wang, Fen
Wang, Xiaofeng
Zhu, Jianfeng
Xiang, Liuyi
ADVANCED ENGINEERING MATERIALS, PTS 1-3, 2011, 194-196 : 1732 - 1735

← 1 2 3 4 5 →