EFFECTS OF TEMPERATURE ON MONOTONIC AND FATIGUE PROPERTIES OF CARBON-FIBER EPOXY CROSS-PLY LAMINATES

被引：2
|
作者：
MATSUHISA, Y [1 ]
KING, JE [1 ]
机构：
[1] UNIV CAMBRIDGE,DEPT MAT SCI & MET,CAMBRIDGE CB2 3QZ,ENGLAND
来源：
JOURNAL DE PHYSIQUE IV | 1993年 / 3卷 / C7期
关键词：
D O I：
10.1051/jp4:19937259
中图分类号：
O4 [物理学];
学科分类号：
0702 ;
摘要：
The effects of test temperature on damage accumulation behaviour has been studied using ''Torayca'' T800H/#3631 in conditions of monotonic and fatigue loading. The damage accumulation behaviour was found to vary as a function of the test temperature, with the effect of temperature on the damage behaviour being different between monotonic and fatigue loading.
引用
收藏
页码：1657 / 1660
页数：4
相关论文
共 50 条
  • [31] Experimental results for fatigue damage growth in laminated fiber reinforced cross-ply laminates
    Sanchez, J. Fernando Rojas
    Waas, Anthony M.
    COMPOSITE STRUCTURES, 2025, 352
  • [32] MONITORING ACOUSTIC-EMISSION IN CROSS-PLY GRAPHITE EPOXY LAMINATES DURING FATIGUE LOADING
    ECKLES, W
    AWERBUCH, J
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1988, 7 (03) : 265 - 283
  • [33] Evaluation of very high cycle fatigue properties for transverse crack initiation in cross-ply carbon fiber-reinforced plastic laminates
    Miyakoshi, Tsuyoshi
    Atsumi, Takeru
    Kosugi, Kensuke
    Hosoi, Atsushi
    Tsuda, Terumasa
    Kawada, Hiroyuki
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2022, 45 (08) : 2403 - 2414
  • [34] MICROSCOPIC FATIGUE DAMAGE PROGRESS IN CFRP CROSS-PLY LAMINATES
    TAKEDA, N
    OGIHARA, S
    KOBAYASHI, A
    COMPOSITES, 1995, 26 (12): : 859 - 867
  • [35] Low velocity impact behavior of glass/epoxy cross-ply laminates with different fiber treatments
    Kessler, Andreas
    Bledzki, Andrzej K.
    Polymer Composites, 1999, 20 (02): : 269 - 278
  • [36] Modelling the transverse cracking in cross-ply laminates: application to fatigue
    Berthelot, JM
    Le Corre, JF
    COMPOSITES PART B-ENGINEERING, 1999, 30 (06) : 569 - 577
  • [37] Low velocity impact behavior of glass/epoxy cross-ply laminates with different fiber treatments
    Kessler, A
    Bledzki, AK
    POLYMER COMPOSITES, 1999, 20 (02) : 269 - 278
  • [38] Statistical fatigue life prediction of cross-ply composite laminates
    Diao, XX
    Ye, L
    Mai, YW
    JOURNAL OF COMPOSITE MATERIALS, 1997, 31 (14) : 1442 - 1460
  • [39] Flexural Fatigue Behavior of Cross-Ply Laminates: An Experimental Approach
    A. R. Bezazi
    A. El Mahi
    J.-M. Berthelot
    B. Bezzazi
    Strength of Materials, 2003, 35 (2) : 149 - 161
  • [40] Microscopic fatigue damage progress in CFRP cross-ply laminates
    Composites, 12 (859):
12345