PROPERTIES OF BI-SR-CA-CU-O HIGH-TC SUPERCONDUCTOR

被引：0
|
作者：
NAIDU, BS
REDDY, BJ
REDDY, YP
REDDY, PJ
机构：
[1] Department of Physics, Sri Venkateswara University, Tirupati
来源：
BULLETIN OF MATERIALS SCIENCE | 1991年 / 14卷 / 02期
关键词：
HIGH-TC SUPERCONDUCTOR; ANNEALING CONDITIONS; SOLID-STATE REACTION; STRUCTURE; RESISTIVITY; AC SUSCEPTIBILITY;
D O I：
10.1007/BF02747317
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of sintering in air and annealing in oxygen flow at various temperatures and times on the superconducting transition of Bi2Sr2Ca1Cu2O8 ceramic was studied. Samples sintered at 1138 K for 24 h in air and slowly-cooled to room temperature are single-phase with the highest zero resistivity temperature of 88 K. XRD pattern showed that the single-phase was characteristic of tetragonal structure with a = 0.5398 nm and c = 3.0620 nm. Both a.c. susceptibility and resistivity measurments give similar values for the onset (100 K) of superconducting transition.
引用
收藏
页码：211 / 216
页数：6
相关论文
共 50 条
  • [31] THE 130 K HIGH-TC SUPERCONDUCTOR IN THE SYSTEM BI-SR-CA-CU-O DOPED WITH SB AND PB
    XU, QL
    MENG, GY
    DONG, Y
    PAN, XJ
    LU, XW
    MAO, ZQ
    YI, D
    CHEN, ZJ
    JIANG, L
    FAN, CG
    GUIEN, Z
    ZHANG, YH
    JOURNAL OF SUPERCONDUCTIVITY, 1990, 3 (02): : 183 - 187
  • [32] HYSTERESIS OF CRITICAL CURRENTS OF A HIGH-TC BI-SR-CA-CU-O SUPERCONDUCTOR IN MAGNETIC-FIELDS
    YAMAMOTO, T
    AOMINE, T
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1988, 27 (10): : L1917 - L1919
  • [33] SYNTHESIS AND DECOMPOSITION OF THE HIGH-TC PHASE OF A PB-DOPED BI-SR-CA-CU-O SUPERCONDUCTOR
    SUZUKI, Y
    INOUE, T
    HAYASHI, S
    KOMATSU, H
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1989, 28 (08): : L1382 - L1384
  • [34] Synchrotron radiation photoelectron spectroscopy of high-Tc superconductor Bi-Sr-Ca-Cu-O single crystals
    Maeda, Fumihiko, 1600, (28):
  • [35] SYNTHESIS OF A HIGH-TC SUPERCONDUCTING PHASE IN BI-SR-CA-CU-O SYSTEM
    MIYASHITA, S
    WAKATA, M
    NOZAKI, A
    EGAWA, K
    OGAMA, T
    YOSHIZAKI, K
    IEEE TRANSACTIONS ON MAGNETICS, 1989, 25 (02) : 2188 - 2191
  • [36] DIAMAGNETIC PROPERTIES OF HIGH-TC BI-SR-CA-CU-O SUPERCONDUCTING THIN-FILMS
    HATTA, S
    ICHIKAWA, Y
    HIROCHI, K
    SETSUNE, K
    ADACHI, H
    WASA, K
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1988, 27 (05): : L855 - L856
  • [37] THE INCOMMENSURATE STRUCTURE OF HIGH-TC SUPERCONDUCTORS IN THE BI-SR-CA-CU-O SYSTEM
    YANG, DY
    LI, JQ
    LI, FH
    ZHOU, YQ
    CHEN, LQ
    HUANG, YZ
    RAN, ZY
    ZHAO, ZX
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1988, 1 (02): : 100 - 101
  • [38] STRUCTURAL, ELECTRICAL AND MAGNETIC-PROPERTIES OF HIGH-TC BI-SR-CA-CU-O SUPERCONDUCTORS
    PRADHAN, AK
    JANA, PC
    ROUL, BK
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1989, 8 (04) : 373 - 375
  • [39] GROWTH OF HIGH-TC BI-SR-CA-CU-O THICK-FILMS
    CHAUDHRY, S
    KHARE, N
    GUPTA, AK
    NAGPAL, KC
    OJHA, VN
    REDDY, GSN
    TOMAR, VS
    BULLETIN OF MATERIALS SCIENCE, 1991, 14 (02) : 521 - 524
  • [40] ON THE MICROSTRUCTURAL EVOLUTION OF SINTERED BI-SR-CA-CU-O HIGH-TC SUPERCONDUCTORS
    ZHANG, JG
    MCCARTNEY, DG
    HUMPHREYS, CJ
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1990, 3 (04): : 185 - 190
12345